UNS R30003 Cold Worked And Aged

Want to keep this datasheet? Save it now in your required format

Ashby charts

See where UNS R30003 Cold Worked And Aged falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

8.4 g/cm³ at 23 °C

Mechanical

Elastic modulus

E

230 GPa at 23 °C

Show Unclassified Cobalt Alloy materials with Elastic modulus of 230 GPa at 23 °C

Elongation

A

10 % at 23 °C

Show Unclassified Cobalt Alloy materials with Elongation of 10 % at 23 °C

Tensile strength

Rm

1740 MPa at 23 °C

Show Unclassified Cobalt Alloy materials with Tensile strength of 1740 MPa at 23 °C

Yield strength

YS

1110 MPa at 23 °C

Show Unclassified Cobalt Alloy materials with Yield strength of 1110 MPa at 23 °C

Thermal

Coefficient of thermal expansion

α

1.3E-5 1/K at 23 °C

Melting point

Tm

1450 °C

Specific heat capacity

cp

450 J/(kg·K) at 23 °C

Thermal conductivity

λ

13 W/(m·K) at 23 °C

Chemical properties

Element

Weight %

Comment

Co

39 - 41 %

Cr

19 - 21 %

Ni

14 - 16 %

Fe

10 - 20.5 %

Mo

6 - 8 %

More

This material data has been provided by MakeItFrom.com.