Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 8.3 g/cm³ Show Material materials with Density of 8.3 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 110 GPa Show Material materials with Elastic modulus of 110 GPa at 23.0 °C | 23.0 °C | |
Elongation | 24 % Show Material materials with Elongation of 24 % at 23.0 °C | 23.0 °C | |
Shear modulus | 40 GPa Show Material materials with Shear modulus of 40 GPa at 23.0 °C | 23.0 °C | Typical for Wrought Copper Brass |
Tensile strength | 440 MPa Show Material materials with Tensile strength of 440 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 190 MPa Show Material materials with Yield strength of 190 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature |
|---|---|---|
Coefficient of thermal expansion | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K at 23.0 °C | 23.0 °C |
Melting point | 890 °C Show Material materials with Melting point of 890 °C | |
Specific heat capacity | 380 J/(kg·K) Show Material materials with Specific heat capacity of 380 J/(kg·K) at 23.0 °C | 23.0 °C |
Thermal conductivity | 120 W/(m·K) Show Material materials with Thermal conductivity of 120 W/(m·K) at 23.0 °C | 23.0 °C |
Chemical properties
| Property | ||
|---|---|---|
Copper | 59 - 62 % | |
Iron | 0 - 0.1 % | |
Lead | 0.4 - 1 % | |
Other | 0 - 0.4 % | |
Tin | 0.5 - 1 % | |
Zinc | 35.5 - 40.1 % |