Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 8.4 g/cm³ Show Material materials with Density of 8.4 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 110 GPa Show Material materials with Elastic modulus of 110 GPa at 23.0 °C | 23.0 °C | |
Elongation | 8 % Show Material materials with Elongation of 8 % at 23.0 °C | 23.0 °C | |
Shear modulus | 40 GPa Show Material materials with Shear modulus of 40 GPa at 23.0 °C | 23.0 °C | Typical for Wrought Copper Brass |
Tensile strength | 520 MPa Show Material materials with Tensile strength of 520 MPa at 23.0 °C | 23.0 °C | |
Yield strength | 440 MPa Show Material materials with Yield strength of 440 MPa at 23.0 °C | 23.0 °C |
Thermal
| Property | Value | Temperature |
|---|---|---|
Coefficient of thermal expansion | 2E-5 1/K Show Material materials with Coefficient of thermal expansion of 2E-5 1/K at 23.0 °C | 23.0 °C |
Melting point | 920 °C Show Material materials with Melting point of 920 °C | |
Specific heat capacity | 380 J/(kg·K) Show Material materials with Specific heat capacity of 380 J/(kg·K) at 23.0 °C | 23.0 °C |
Thermal conductivity | 120 W/(m·K) Show Material materials with Thermal conductivity of 120 W/(m·K) at 23.0 °C | 23.0 °C |
Chemical properties
| Property | ||
|---|---|---|
Bismuth | 0 - 5.9E-3 % | |
Copper | 68.5 - 71.5 % | |
Iron | 0 - 0.05 % | |
Lead | 0 - 0.07 % | |
Other | 0 - 0.3 % | |
Zinc | 28.1 - 31.5 % |