PHOENIX™ 08301 fully hydrogenated SEBS (Styrene Ethylene Butylene Styrene) + SBS (Styrene Butadiene Styrene) compound

Alternative and trade names
THERMOLAST®, Monprene®, Versaflex™, Dryflex®
.XLSX
.PDF
Save

Description

This grade is an easy processing Thermoplastic Elastomer (TPE) designed for injection molding. The key features are: Easy to process and color, overmoldable to Polypropylene, soft touch, rubber like texture and feel, good elasticity, non toxic

Properties

General

Density ρ

1.03 - 1.09 g/cm³ at 20 °C

ASTM D792

Melt mass-flow rate MFR

68.2 g/10min at 20 °C

ASTM D1238 (190°C, 2.16kg)

Shrinkage cshrink

1.5 - 2.1 % at 20 °C

ASTM D955

Shrinkage, transverse cshrink, trans

1.4 - 2 % at 20 °C

ASTM D955

Mechanical

Elongation A

609.2 % at 20 °C

ASTM D412 (500 mm/min)

Hardness, Shore A HS A

27 - 33 [-] at 20 °C

ASTM D2240

Modulus at 100% elongation EA=100

5.780710000000001E-4 GPa at 20 °C

ASTM D412 (500 mm/min)

Modulus at 300% elongation EA=300

9.72179E-4 GPa at 20 °C

ASTM D412 (500 mm/min)

Tear strength Rtear

8.51 kN/m at 20 °C

ASTM D624 Die C (500 mm/min)

Tensile strength Rm

1.65 MPa at 20 °C

ASTM D412 (500 mm/min)

Technological properties

Application areas

Bicycle grip, toothbrush, razor grip

Color

White

Processing methods

Injection molding

This material data has been provided by Phon Tech.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.