General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.77 g/cm³ Show Supplier Material materials with Density of 1.77 g/cm³ | ISO 1183 |
Water absorption | 23.0 °C | 0.03 % Show Supplier Material materials with Water absorption of 0.03 % | ISO 62 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elongation | 23.0 °C | 1.3 % Show Supplier Material materials with Elongation of 1.3 % | ISO 527 |
Flexural modulus | 23.0 °C | 15 GPa Show Supplier Material materials with Flexural modulus of 15 GPa | ISO 178 |
Flexural strength | 23.0 °C | 240 MPa Show Supplier Material materials with Flexural strength of 240 MPa | ISO 178 |
Impact strength, Charpy notched | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 9 kJ/m² | ISO 179 |
Tensile strength | 23.0 °C | 155 MPa Show Supplier Material materials with Tensile strength of 155 MPa | ISO 527 |
Thermal
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 260 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 260 °C | ISO 75 | |
Max service temperature | 260 °C Show Supplier Material materials with Max service temperature of 260 °C | ||
Melting point | 280 °C Show Supplier Material materials with Melting point of 280 °C | ISO 11357 (10°C/min) | |
Flammability | V-0, UL-94 |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 150 V Show Supplier Material materials with Comparative tracking index of 150 V | IEC 60112 |
Dielectric constant | 23.0 °C | 4.2 [-] Show Supplier Material materials with Dielectric constant of 4.2 [-] | IEC 60250 |
Dielectric strength | 23.0 °C | 16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm | IEC 60243 |
Dissipation factor | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor of 2E-3 [-] | IEC 60250 |
Volume resistivity | 23.0 °C | 2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm | IEC 60093 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in the production of gear, bearing, slide and low friction coefficient, low friction consumption | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |