PPS GF45 SG451T65

Alternative and trade names
PPS-SG451T65

Want to keep this datasheet? Save it now in your required format

Description

It is a 45% glass fiber reinforced linear polyphenylene sulfide compound developed to provide excellent engineering properties and processability.

This material data has been provided by Sciengy New Materials Co. Ltd.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.7 g/cm³ Show Supplier Material materials with Density of 1.7 g/cm³	ISO 1183
Water absorption	23.0 °C	0.02 % Show Supplier Material materials with Water absorption of 0.02 %	ISO 62

Mechanical

Property	Temperature	Value	Comment
Elongation	23.0 °C	1.7 % Show Supplier Material materials with Elongation of 1.7 %	ISO 527
Flexural modulus	23.0 °C	16 GPa Show Supplier Material materials with Flexural modulus of 16 GPa	ISO 178
Flexural strength	23.0 °C	260 MPa Show Supplier Material materials with Flexural strength of 260 MPa	ISO 178
Impact strength, Charpy notched	23.0 °C	10 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 10 kJ/m²	ISO 179
Tensile strength	23.0 °C	170 MPa Show Supplier Material materials with Tensile strength of 170 MPa	ISO 527

Thermal

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	260 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 260 °C	ISO 75
Melting point	280 °C Show Supplier Material materials with Melting point of 280 °C	ISO 11357 (10°C/min)
Flammability	V-0, UL-94

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	155 V Show Supplier Material materials with Comparative tracking index of 155 V	IEC 60112
Dielectric constant	23.0 °C	4.5 [-] Show Supplier Material materials with Dielectric constant of 4.5 [-]	IEC 60250
Dielectric strength	23.0 °C	16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm	IEC 60243
Dissipation factor	23.0 °C	2E-3 [-] Show Supplier Material materials with Dissipation factor of 2E-3 [-]	IEC 60250
Volume resistivity	23.0 °C	2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm	IEC 60093

Technological properties

Property
Application areas	Can be used in auto parts such as thermostat housing,water pump cap,regulator,and other industrial fileds.
Fillers	45% Glass Fiber
Processing methods	Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min