General
Property | Temperature | Value | Comment |
---|---|---|---|
Bio-based content | 40.0 % Show Supplier Material materials with Bio-based content of 40.0 % | ||
Density | 23 °C | 1.06 g/cm³ Show Supplier Material materials with Density of 1.06 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23 °C | 2.2 GPa Show Supplier Material materials with Elastic modulus of 2.2 GPa | ISO 527-2/2 |
Elongation | 23 °C | 7.3 % Show Supplier Material materials with Elongation of 7.3 % | ISO 527-2/50 |
Flexural modulus | 23 °C | 1.9 GPa Show Supplier Material materials with Flexural modulus of 1.9 GPa | ISO 527-2/2 |
Impact strength, Charpy unnotched | 23 °C | 24 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 24 kJ/m² | ISO 179/1eU |
Tensile strength | 23 °C | 28 MPa Show Supplier Material materials with Tensile strength of 28 MPa | ISO 527-2/50 |
Thermal
Property | Value |
---|---|
Flammability | UL94: HB |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 23 °C | 15 g/10min Show Supplier Material materials with Melt mass-flow rate of 15 g/10min | ISO 1133, 220°C/5kg |
Technological properties
Property | ||
---|---|---|
Certifications | ||
Fillers | 40% S-Wood Fiber | |
Other | General safety instructions, read also Process instructions: | |
Processing methods | Drying: 2 hours at 90°C Injection moulding machine Temperatures: The below instructions may differ on due to injection speed, machine etc. Read process intructions. |