General
Property | Temperature | Value | Comment |
---|---|---|---|
Bio-based content | 30.0 % Show Supplier Material materials with Bio-based content of 30.0 % | ||
Density | 23 °C | 1.02 g/cm³ Show Supplier Material materials with Density of 1.02 g/cm³ | ISO 1183 |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23 °C | 3.4 GPa Show Supplier Material materials with Elastic modulus of 3.4 GPa | ISO 527-2/2 |
Elongation | 23 °C | 3.6 % Show Supplier Material materials with Elongation of 3.6 % | ISO 527-2/50 |
Flexural modulus | 23 °C | 2.8 GPa Show Supplier Material materials with Flexural modulus of 2.8 GPa | ISO 527-2/2 |
Impact strength, Charpy unnotched | 23 °C | 19 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 19 kJ/m² | ISO 179/1eU |
Tensile strength | 23 °C | 41 MPa Show Supplier Material materials with Tensile strength of 41 MPa | ISO 527-2/50 |
Thermal
Property | Value |
---|---|
Flammability | UL94: HB |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 23 °C | 12 g/10min Show Supplier Material materials with Melt mass-flow rate of 12 g/10min | ISO 1133, 220°C/5kg |
Technological properties
Property | ||
---|---|---|
Certifications | ||
Fillers | 30% T-Wood Fiber | |
Other | General safety instructions, read also Process instructions: | |
Processing methods | Drying: 2 hours at 105°C Injection moulding machine Temperatures: The below instructions may differ on due to injection speed, machine etc. Read process intructions. |