Primary standard name
Equivalent standard names
Related standards
Chemical composition
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Material Information
Certifications
Food Contact,Yellow Card
-
USDA Certified Bio-based product
<li>Chemical substances: REACH Compliant</li> <li>Raw material: FSC/PEFC™ Chain of Custody</li> <li>
<p>FOOD CONTACT STATUS: In the European Union, Luminy® PLA polymers are compliant with EU commission
Handling recommendations
-
Store at room temperature (18-27°C / 65-80°F), out of direct heat and sunlight, and in a dry place.
-
-
-
Processing Tag
Chemical composition
-
Biodegradable batch based on PLA, contains copolyester and additives.
-
-
-
Filler Type
-
-
-
-
Fillers
-
-
-
40% L-Wood Fiber
-
Color
-
-
-
-
Crystalline White
Certification Groups
-
Processing methods
<p>Injection Molding:</p> <li>Typical melt temperature (Min / Recommended / Max) : 210°C / 230°C
-
-
<p>Drying: 2 hours at 105°C</p> <p>Injection moulding machine Temperatures:</p> <li>Nozzle t
<p>Luminy® LX530 can be processed on conventional extrusion spinning and drawing equipment. Thorough
Application areas
Accessories
This material contains wood fibres, and imitates wood in terms of its smell and aesthetic.
NuPlastiQ® BC 27240 is intended for bags and film applications that require at least 40% bio-content
-
PLA extruded filament for FDM/FFF 3D printing, single-serve capsules for coffee machine, injection m
Other
-
-
-
<p>General safety instructions, read also Process instructions:</p> <li>Avoid high temperatures an l
<p>NOTICE REGARDING USE RESTRICTIONS: Unless specifically agreed to in writing, Total Corbion PLA wi
Mechanical
Impact strength, Charpy notched, Ivnot
4 kJ/m² at -30 °C
-
-
-
5 kJ/m² at 23 °C
Hardness, Shore D, HS D
68 [-] at 23 °C
-
-
-
-
Flexural modulus, Ebend
-
3.2 GPa at 23 °C
0.24 GPa at 23 °C
4 GPa at 23 °C
-
Elongation at yield, Ay
5 % at 23 °C
-
-
-
-
Flexural strength, σbend
-
43 MPa at 23 °C
-
-
-
Elongation, A
50 % at 23 °C
-
272 % at 23 °C
3.5 % at 23 °C
5 % at 23 °C
Elastic modulus, E
1.3 GPa at 23 °C
-
0.2 GPa at 23 °C
4.2 GPa at 23 °C
3.5 GPa at 23 °C
Tensile strength, Rm
-
40 MPa at 23 °C
12 MPa at 23 °C
49 MPa at 23 °C
50 MPa at 23 °C
Impact strength, Charpy unnotched, Iunnot
-
-
21 kJ/m² at 23 °C
-
Yield strength, YS
41 MPa at 23 °C
-
-
-
-
General
Residual monomer, cmono
-
-
-
-
0.3 mg/kg at 23 °C
Density, ρ
1.03 g/cm³ at 23 °C
1.23 g/cm³ at 23 °C
1.3 g/cm³ at 23 °C
1.06 g/cm³ at 23 °C
1.24 g/cm³ at 23 °C
Water content, cwater,cont
-
-
-
-
0.04 % at 23 °C
Water absorption, cwater
1.9 % at 23 °C
-
-
-
-
Bio-based content, Bio%
100 %
100 %
100 %
100 %
100 %
Carbon Footprint
-
-
0.2
-
-
Rheological Properties
Shrinkage, transverse, cshrink, trans
0.8 % at 23 °C
-
-
-
-
Shrinkage, cshrink
0.4 % at 23 °C
-
-
-
-
Melt volume-flow rate, MVR
11 cm³/10min
-
-
-
-
Melt mass-flow rate, MFR
-
22 g/10min
3.7 g/10min
15 g/10min
23 g/10min
Thermal
Vicat softening temperature, Tsoft
-
48 °C
-
-
-
Glass transition temperature, Tg
-
-
-
-
60 °C
Flammability
At thickness 1.5 mm IEC 60695-11-10: HB and yellow card available
-
-
UL94: HB
-
Heat deflection temperature, 0.45 MPa, HDT0.45,MPa
-
-
-
-
60 °C
Heat deflection temperature, HDT
-
-
-
-
60 °C
Melting point, Tm
189 °C
150 - 170 °C
140 - 160 °C
-
165 °C