extrudr Wood Filament

Alternative and trade names
extrudr Wood Filament

Want to keep this datasheet? Save it now in your required format

Description

This wood material is made from lignin and another biopolymer.

This material data has been provided by extrudr.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

All categories

Applications

Manufacturing

Additive Manufacturing

Fused Filament Fabrication (Fff)

Materials by this supplier

extrudr PETG Filament

extrudr PLA NX1 Filament

extrudr ABS Filament

extrudr DuraPro ASA Filament

extrudr GREENTEC PRO Carbon

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Bio-based content		100 % Show Supplier Material materials with Bio-based content of 100 %
Density	23.0 °C	1.23 g/cm³ Show Supplier Material materials with Density of 1.23 g/cm³	ISO 2781

Mechanical

Property	Temperature	Value	Comment
Flexural modulus	23.0 °C	3.2 GPa Show Supplier Material materials with Flexural modulus of 3.2 GPa	ISO 527
Flexural strength	23.0 °C	43 MPa Show Supplier Material materials with Flexural strength of 43 MPa	ISO 527
Tensile strength	23.0 °C	40 MPa Show Supplier Material materials with Tensile strength of 40 MPa	ISO 527

Thermal

Property	Value	Comment
Melting point	150 - 170 °C Show Supplier Material materials with Melting point of 150 - 170 °C
Vicat softening temperature	48 °C Show Supplier Material materials with Vicat softening temperature of 48 °C	ISO 306

Rheological Properties

Property	Value	Comment
Melt mass-flow rate	22 g/10min Show Supplier Material materials with Melt mass-flow rate of 22 g/10min	ISO 1133

Technological properties

Property
Application areas	This material contains wood fibres, and imitates wood in terms of its smell and aesthetic.
Chemical composition	Biodegradable batch based on PLA, contains copolyester and additives.
Handling recommendations	Store at room temperature (18-27°C / 65-80°F), out of direct heat and sunlight, and in a dry place. When stored correctly, this material has a shelf life of 1 year