Primary standard name
Equivalent standard names
Related standards
Chemical composition
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Element
Weight %
Comment
Material Information
Certifications
-
USDA Certified Bio-based product
Food Contact: Halal
Food Contact: Halal
Food Contact: Halal
Food Contact: Halal
<p>FOOD CONTACT STATUS: In the European Union, Luminy® PLA polymers are compliant with EU commission
Handling recommendations
Store at room temperature (18-27°C / 65-80°F), out of direct heat and sunlight, and in a dry place.
-
-
-
-
-
-
Processing Tag
Chemical composition
Biodegradable batch based on PLA, contains copolyester and additives.
-
-
-
-
-
-
Color
-
-
-
-
-
-
Crystalline White
Certification Groups
-
Processing methods
-
-
1. Clean extruder with general purpose polyethylene or polypropylene. 2. Vacuum out hopper system to
1. Clean extruder with general purpose polyethylene or polypropylene. 2. Vacuum out hopper system to
1. Purge the machine using LDPE/HDPE material at original processing temperature. 2. Lower the tempe
1. Pre-clean the machine with LDPE at original processing temperature. 2. Purge the machine using BM
<p>Luminy® LX530 can be processed on conventional extrusion spinning and drawing equipment. Thorough
Application areas
This material contains wood fibres, and imitates wood in terms of its smell and aesthetic.
NuPlastiQ® BC 27240 is intended for bags and film applications that require at least 40% bio-content
Molded products, high impact , crate, container, pails.
Toy, tube, profile extrusion
Straw, tube
Shopping bag, garbage bag, mulch film, waste bag, food packaging bag
PLA extruded filament for FDM/FFF 3D printing, single-serve capsules for coffee machine, injection m
Other
-
-
-
-
-
-
<p>NOTICE REGARDING USE RESTRICTIONS: Unless specifically agreed to in writing, Total Corbion PLA wi
Mechanical
Impact strength, Charpy notched, Ivnot
-
-
-
-
-
-
5 kJ/m² at 23 °C
Hardness, Shore D, HS D
-
-
64 [-] at 23 °C
64 [-] at 23 °C
70 [-] at 23 °C
-
-
Flexural modulus, Ebend
3.2 GPa at 23 °C
0.24 GPa at 23 °C
0.48 GPa at 23 °C
4.43 GPa at 23 °C
2 GPa at 23 °C
-
-
Flexural strength, σbend
43 MPa at 23 °C
-
21 MPa at 23 °C
14 MPa at 23 °C
65 MPa at 23 °C
-
-
Elongation, A
-
272 % at 23 °C
59 % at 23 °C
89 % at 23 °C
30 % at 23 °C
300 % at 23 °C
5 % at 23 °C
Elastic modulus, E
-
0.2 GPa at 23 °C
-
-
-
-
3.5 GPa at 23 °C
Tensile strength, Rm
40 MPa at 23 °C
12 MPa at 23 °C
14 MPa at 23 °C
9 MPa at 23 °C
40 MPa at 23 °C
40 MPa at 23 °C
50 MPa at 23 °C
Impact strength, Izod unnotched, ASTM, IIzod,unnot,astm
-
-
50 J/m at 23 °C
38 J/m at 23 °C
20 J/m at 23 °C
-
-
General
Residual monomer, cmono
-
-
-
-
-
-
0.3 mg/kg at 23 °C
Density, ρ
1.23 g/cm³ at 23 °C
1.3 g/cm³ at 23 °C
1.11 g/cm³ at 23 °C
1.1 g/cm³ at 23 °C
1.3 g/cm³ at 23 °C
1.26 - 1.3 g/cm³ at 23 °C
1.24 g/cm³ at 23 °C
Water content, cwater,cont
-
-
-
-
-
-
0.04 % at 23 °C
Bio-based content, Bio%
100 %
100 %
100 %
100 %
100 %
100 %
100 %
Carbon Footprint
-
0.2
-
-
-
-
-
Rheological Properties
Melt mass-flow rate, MFR
22 g/10min
3.7 g/10min
33 g/10min
9 g/10min
8 g/10min
5 g/10min
23 g/10min
Thermal
Decomposition heat, Qdecompose
-
-
-
185 J/g
220 J/g
-
-
Vicat softening temperature, Tsoft
48 °C
-
-
-
-
-
-
Glass transition temperature, Tg
-
-
-
-
-
-
60 °C
Heat deflection temperature, 0.45 MPa, HDT0.45,MPa
-
-
-
-
-
-
60 °C
Max service temperature, Tmax
-
-
185 °C
185 °C
-
-
-
Heat deflection temperature, HDT
-
-
-
-
-
-
60 °C
Melting point, Tm
150 - 170 °C
140 - 160 °C
165 °C
132 °C
140 °C
110 - 120 °C
165 °C