Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dichte | 1.97 g/cm³ Show Supplier Material materials with Dichte of 1.97 g/cm³ | dry | ISO 1183 | |
Wasserabsorption | 0.03 % Show Supplier Material materials with Wasserabsorption of 0.03 % | dry | ISO 62 | at 23°C after 24h |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Biegemodul | 20 GPa Show Supplier Material materials with Biegemodul of 20 GPa | dry | ISO 178 | |
120 °C | 14 GPa Show Supplier Material materials with Biegemodul of 14 GPa | dry | ISO 178 | |
160 °C | 9.1 GPa Show Supplier Material materials with Biegemodul of 9.1 GPa | dry | ISO 178 | |
200 °C | 7 GPa Show Supplier Material materials with Biegemodul of 7 GPa | dry | ISO 178 | |
Dehnung | -40 °C | 1 % Show Supplier Material materials with Dehnung of 1 % | dry | ISO 527-1/-2 |
1 % Show Supplier Material materials with Dehnung of 1 % | dry | ISO 527-1/-2 | ||
120 °C | 1.7 % Show Supplier Material materials with Dehnung of 1.7 % | dry | ISO 527-1/-2 | |
160 °C | 2.4 % Show Supplier Material materials with Dehnung of 2.4 % | dry | ISO 527-1/-2 | |
180 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | dry | ISO 527-1/-2 | |
200 °C | 2.5 % Show Supplier Material materials with Dehnung of 2.5 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | -40 °C | 23 GPa Show Supplier Material materials with Elastizitätsmodul of 23 GPa | dry | ISO 527-1/-2 |
20 GPa Show Supplier Material materials with Elastizitätsmodul of 20 GPa | dry | ISO 527-1/-2 | ||
120 °C | 11 GPa Show Supplier Material materials with Elastizitätsmodul of 11 GPa | dry | ISO 527-1/-2 | |
160 °C | 8.9 GPa Show Supplier Material materials with Elastizitätsmodul of 8.9 GPa | dry | ISO 527-1/-2 | |
180 °C | 8 GPa Show Supplier Material materials with Elastizitätsmodul of 8 GPa | dry | ISO 527-1/-2 | |
200 °C | 7.7 GPa Show Supplier Material materials with Elastizitätsmodul of 7.7 GPa | dry | ISO 527-1/-2 | |
Flexural yield strength | 230 MPa Show Supplier Material materials with Flexural yield strength of 230 MPa | dry | ISO 178 | |
120 °C | 150 MPa Show Supplier Material materials with Flexural yield strength of 150 MPa | dry | ISO 178 | |
160 °C | 110 MPa Show Supplier Material materials with Flexural yield strength of 110 MPa | dry | ISO 178 | |
200 °C | 85 MPa Show Supplier Material materials with Flexural yield strength of 85 MPa | dry | ISO 178 | |
Hardness, Rockwell R | 120 [-] Show Supplier Material materials with Hardness, Rockwell R of 120 [-] | dry | ISO 2039-2 | |
Härte, Rockwell M | 101 [-] Show Supplier Material materials with Härte, Rockwell M of 101 [-] | dry | ISO 2039-2 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 6.8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 6.8 kJ/m² | dry | ISO 179/1eA |
23 °C | 6.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 6.5 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 27 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 27 kJ/m² | dry | ISO 179/1eU |
23 °C | 25 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 25 kJ/m² | dry | ISO 179/1eU | |
Zugfestigkeit | -40 °C | 165 MPa Show Supplier Material materials with Zugfestigkeit of 165 MPa | dry | ISO 527-1/-2 |
145 MPa Show Supplier Material materials with Zugfestigkeit of 145 MPa | dry | ISO 527-1/-2 | ||
120 °C | 98 MPa Show Supplier Material materials with Zugfestigkeit of 98 MPa | dry | ISO 527-1/-2 | |
160 °C | 75 MPa Show Supplier Material materials with Zugfestigkeit of 75 MPa | dry | ISO 527-1/-2 | |
180 °C | 70 MPa Show Supplier Material materials with Zugfestigkeit of 70 MPa | dry | ISO 527-1/-2 | |
200 °C | 62 MPa Show Supplier Material materials with Zugfestigkeit of 62 MPa | dry | ISO 527-1/-2 |
Thermisch
Property | Value | Condition | Thickness | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|---|
Entflammbarkeit | V-0 | dry | 1.5 mm | IEC 60695-11-10 | UL recognition :Yes | |
Glasübergangstemperatur | 90 °C Show Supplier Material materials with Glasübergangstemperatur of 90 °C | dry | ISO 11357-1/-2 | 10°C/min | ||
Koeffizient der thermischen Ausdehnung | 1.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | ||
1.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.5e-07 1/K | dry | ISO 11359-1/-2 | parallel, above Tg | |||
2.7e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.7e-07 1/K | dry | ISO 11359-1/-2 | Normal | |||
7.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 7.5e-07 1/K | dry | ISO 11359-1/-2 | normal, above Tg | |||
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | dry | 0.7 mm | UL746B | ||
Relative temperature index, mechanical impact | 130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C | dry | 0.7 mm | UL746B | ||
Relative temperature index, mechanical strength | 130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C | dry | 0.7 mm | UL746B | ||
Schmelzpunkt | 280 °C Show Supplier Material materials with Schmelzpunkt of 280 °C | dry | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 230 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 230 °C | dry | ISO 75-1/-2 | 8 MPa | ||
277 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 277 °C | dry | ISO 75-1/-2 | 2 MPa | |||
Wärmeleitfähigkeit | 0.7 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.7 W/(m·K) | dry | ASTM E1461 | in plane | ||
0.7 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 0.7 W/(m·K) | dry | ASTM E1461 | through plane |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dielektrizitätskonstante | 5 [-] Show Supplier Material materials with Dielektrizitätskonstante of 5 [-] | dry | IEC 60250 | 1GHz |
5 [-] Show Supplier Material materials with Dielektrizitätskonstante of 5 [-] | dry | IEC 60250 | 5GHz | |
Durchschlagfestigkeit | 25 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 25 kV/mm | dry | IEC 60243-1 | |
Kriechstromfestigkeit | 225 V Show Supplier Material materials with Kriechstromfestigkeit of 225 V | dry | IEC 60112 | |
Surface resistivity | 1e+15 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq | dry | IEC 62631-3-2 | |
Verlustfaktor | 34 [-] Show Supplier Material materials with Verlustfaktor of 34 [-] | dry | IEC 60250 | 1GHz |
44 [-] Show Supplier Material materials with Verlustfaktor of 44 [-] | dry | IEC 60250 | 5GHz | |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Crankshaft Covers, Coil insulation, Rectifier, Water pump part, Alternator bridges, Thermal management valve bodies | |
Fillers | 65% Glass Fiber and Mineral Powder |