Property | Value | Condition | Testing Standard |
---|---|---|---|
Dichte | 1.11 g/cm³ Show Supplier Material materials with Dichte of 1.11 g/cm³ | dry | ISO 1183 |
Moisture absorption | 3.2 % Show Supplier Material materials with Moisture absorption of 3.2 % | dry | Sim. to ISO 62 |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Biegemodul | 2 GPa Show Supplier Material materials with Biegemodul of 2 GPa | dry | ISO 178 | |
2.2 GPa Show Supplier Material materials with Biegemodul of 2.2 GPa | conditioned | ISO 178 | ||
Dehnung | 20 % Show Supplier Material materials with Dehnung of 20 % | dry | ISO 527-1/-2 | |
28.0 % Show Supplier Material materials with Dehnung of 28.0 % | conditioned | ISO 527-1/-2 | ||
100 °C | 20 % Show Supplier Material materials with Dehnung of 20 % | dry | ISO 527-1/-2 | |
120 °C | 20 % Show Supplier Material materials with Dehnung of 20 % | dry | ISO 527-1/-2 | |
140 °C | 38 % Show Supplier Material materials with Dehnung of 38 % | dry | ISO 527-1/-2 | |
160 °C | 84 % Show Supplier Material materials with Dehnung of 84 % | dry | ISO 527-1/-2 | |
200 °C | 92 % Show Supplier Material materials with Dehnung of 92 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | 2.1 GPa Show Supplier Material materials with Elastizitätsmodul of 2.1 GPa | dry | ISO 527-1/-2 | |
2.3 GPa Show Supplier Material materials with Elastizitätsmodul of 2.3 GPa | conditioned | ISO 527-1/-2 | ||
100 °C | 1.7 GPa Show Supplier Material materials with Elastizitätsmodul of 1.7 GPa | dry | ISO 527-1/-2 | |
120 °C | 1.6 GPa Show Supplier Material materials with Elastizitätsmodul of 1.6 GPa | dry | ISO 527-1/-2 | |
140 °C | 0.9 GPa Show Supplier Material materials with Elastizitätsmodul of 0.9 GPa | dry | ISO 527-1/-2 | |
160 °C | 0.3 GPa Show Supplier Material materials with Elastizitätsmodul of 0.3 GPa | dry | ISO 527-1/-2 | |
200 °C | 0.27 GPa Show Supplier Material materials with Elastizitätsmodul of 0.27 GPa | dry | ISO 527-1/-2 | |
Elongation at yield | 5 % Show Supplier Material materials with Elongation at yield of 5 % | conditioned | ISO 527-1/-2 | |
7.5 % Show Supplier Material materials with Elongation at yield of 7.5 % | dry | ISO 527-1/-2 | ||
Flexural yield strength | 90 MPa Show Supplier Material materials with Flexural yield strength of 90 MPa | dry, conditioned | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 30 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 30 kJ/m² | dry | ISO 179/1eA |
23 °C | 40 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 40 kJ/m² | dry | ISO 179/1eA | |
Streckgrenze | 54 MPa Show Supplier Material materials with Streckgrenze of 54 MPa | conditioned | ISO 527-1/-2 | |
64 MPa Show Supplier Material materials with Streckgrenze of 64 MPa | dry | ISO 527-1/-2 | ||
120 °C | 32 MPa Show Supplier Material materials with Streckgrenze of 32 MPa | dry | ISO 527-1/-2 | |
Zugfestigkeit | 50 MPa Show Supplier Material materials with Zugfestigkeit of 50 MPa | conditioned | ISO 527-1/-2 | |
60 MPa Show Supplier Material materials with Zugfestigkeit of 60 MPa | dry | ISO 527-1/-2 | ||
100 °C | 36 MPa Show Supplier Material materials with Zugfestigkeit of 36 MPa | dry | ISO 527-1/-2 | |
120 °C | 32 MPa Show Supplier Material materials with Zugfestigkeit of 32 MPa | dry | ISO 527-1/-2 | |
140 °C | 24 MPa Show Supplier Material materials with Zugfestigkeit of 24 MPa | dry | ISO 527-1/-2 | |
160 °C | 21 MPa Show Supplier Material materials with Zugfestigkeit of 21 MPa | dry | ISO 527-1/-2 | |
200 °C | 14.0 MPa Show Supplier Material materials with Zugfestigkeit of 14.0 MPa | dry | ISO 527-1/-2 |
Thermisch
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Glasübergangstemperatur | 150 °C Show Supplier Material materials with Glasübergangstemperatur of 150 °C | dry | ASTM D5026/D7028 | DMTA (tan d) | |
Schmelzpunkt | 335 °C Show Supplier Material materials with Schmelzpunkt of 335 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 135 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 135 °C | dry | ISO 75-1/-2 | 2 MPa | |
160 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 160 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Rheological Properties
Technological properties
Property |
---|