Stanyl® TW250F6

Alternative und Handelsbezeichungen
PA46-GF30 FR(17)

Want to keep this datasheet? Save it now in your required format

Description

Stanyl® is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl® is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.

Datasheet URL:

Stanyl® TW250F6

Diese Materialdaten wurden von DSM zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Value	Condition	Testing Standard	Comment
Dichte	1.67 g/cm³ Show Supplier Material materials with Dichte of 1.67 g/cm³	dry	ISO 1183
Moisture absorption	1.8 % Show Supplier Material materials with Moisture absorption of 1.8 %	dry	Sim. to ISO 62
Sauerstoffindex	37 % Show Supplier Material materials with Sauerstoffindex of 37 %	dry	ISO 4589-1/-2
Wasserabsorption	1.7 % Show Supplier Material materials with Wasserabsorption of 1.7 %	dry	ISO 62	at 23°C after 24h
	5.9 % Show Supplier Material materials with Wasserabsorption of 5.9 %	dry	Sim. to ISO 62

Mechanisch

Property	Temperature	Value	Condition	Testing Standard	Thickness	Comment
Biegemodul		7.3 GPa Show Supplier Material materials with Biegemodul of 7.3 GPa	conditioned	ISO 178
		11 GPa Show Supplier Material materials with Biegemodul of 11 GPa	dry	ISO 178
	120 °C	6.5 GPa Show Supplier Material materials with Biegemodul of 6.5 GPa	dry	ISO 178
	160 °C	5 GPa Show Supplier Material materials with Biegemodul of 5 GPa	dry	ISO 178
Dehnung		2.4 % Show Supplier Material materials with Dehnung of 2.4 %	dry	ISO 527-1/-2
		2.4 % Show Supplier Material materials with Dehnung of 2.4 %	dry	ISO 527-1/-2	1 mm
		3.5 % Show Supplier Material materials with Dehnung of 3.5 %	conditioned	ISO 527-1/-2
	120 °C	4 % Show Supplier Material materials with Dehnung of 4 %	dry	ISO 527-1/-2
	160 °C	4 % Show Supplier Material materials with Dehnung of 4 %	dry	ISO 527-1/-2
Elastizitätsmodul		8 GPa Show Supplier Material materials with Elastizitätsmodul of 8 GPa	conditioned	ISO 527-1/-2
		12 GPa Show Supplier Material materials with Elastizitätsmodul of 12 GPa	dry	ISO 527-1/-2
		12 GPa Show Supplier Material materials with Elastizitätsmodul of 12 GPa	dry	ISO 527-1/-2	1 mm
	120 °C	7.5 GPa Show Supplier Material materials with Elastizitätsmodul of 7.5 GPa	dry	ISO 527-1/-2
	160 °C	6.2 GPa Show Supplier Material materials with Elastizitätsmodul of 6.2 GPa	dry	ISO 527-1/-2
Flexural yield strength		190 MPa Show Supplier Material materials with Flexural yield strength of 190 MPa	conditioned	ISO 178
		260 MPa Show Supplier Material materials with Flexural yield strength of 260 MPa	dry	ISO 178
	120 °C	170 MPa Show Supplier Material materials with Flexural yield strength of 170 MPa	dry	ISO 178
	160 °C	140 MPa Show Supplier Material materials with Flexural yield strength of 140 MPa	dry	ISO 178
Schlagfestigkeit, Charpy gekerbt	-30 °C	10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m²	dry, conditioned	ISO 179/1eA
	23 °C	11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m²	dry, conditioned	ISO 179/1eA
Schlagzähigkeit, Charpy ungekerbt	-30 °C	50 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 50 kJ/m²	dry, conditioned	ISO 179/1eU
	23 °C	60 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 60 kJ/m²	dry, conditioned	ISO 179/1eU
Zugfestigkeit		120 MPa Show Supplier Material materials with Zugfestigkeit of 120 MPa	conditioned	ISO 527-1/-2
		180 MPa Show Supplier Material materials with Zugfestigkeit of 180 MPa	dry	ISO 527-1/-2
		180 MPa Show Supplier Material materials with Zugfestigkeit of 180 MPa	dry	ISO 527-1/-2	1 mm	at low thickness
	120 °C	105 MPa Show Supplier Material materials with Zugfestigkeit of 105 MPa	dry	ISO 527-1/-2
	160 °C	95 MPa Show Supplier Material materials with Zugfestigkeit of 95 MPa	dry	ISO 527-1/-2

Thermisch

Property	Value	Condition	Thickness	Testing Standard	Pressure	Comment
Entflammbarkeit	V-0	dry	1.5 mm	IEC 60695-11-10		UL recognition :Yes
Glasübergangstemperatur	75 °C Show Supplier Material materials with Glasübergangstemperatur of 75 °C	dry		ISO 11357-1/-2		10°C/min
Glow Wire Flammability Index	960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C	dry	3 mm	IEC 60695-2-12
	960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C	dry	0.75 mm	IEC 60695-2-12
Glow Wire Ignition Temperature	800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C	dry	0.75 mm	IEC 60695-2-13
	925 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 925 °C	dry	3 mm	IEC 60695-2-13
Koeffizient der thermischen Ausdehnung	2.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.5e-07 1/K	dry		ISO 11359-1/-2		Parallel
	5.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 5.5e-07 1/K	dry		ISO 11359-1/-2		Normal
Relative temperature index, electrical	140 °C Show Supplier Material materials with Relative temperature index, electrical of 140 °C	dry	0.75 mm	UL746B
Relative temperature index, mechanical impact	120 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 120 °C	dry	0.75 mm	UL746B
Relative temperature index, mechanical strength	130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C	dry	0.75 mm	UL746B
Schmelzpunkt	295 °C Show Supplier Material materials with Schmelzpunkt of 295 °C	dry		ISO 11357-1/-3		10°C/min
Temperaturleitfähigkeit	1.11e-07 mm²/s Show Supplier Material materials with Temperaturleitfähigkeit of 1.11e-07 mm²/s	dry		-
Vicat-Erweichungstemperatur	290 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 290 °C	dry		ISO 306		50°C/h 50N
Wärmeformbeständigkeitstemperatur	290 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 290 °C	dry		ISO 75-1/-2	2 MPa
	290 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 290 °C	dry		ISO 75-1/-2	0.45 MPa

Elektrisch

Property	Value	Condition	Testing Standard
Durchschlagfestigkeit	30 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 30 kV/mm	dry	IEC 60243-1
Kriechstromfestigkeit	175 V Show Supplier Material materials with Kriechstromfestigkeit of 175 V	dry	IEC 60112
Surface resistivity	1e+13 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+13 Ω/sq	conditioned	IEC 62631-3-2
Volume resistivity	1e+06 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+06 Ω·cm	conditioned	IEC 62631-3-1
	1e+12 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm	dry	IEC 62631-3-1

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Density of melt	1450 g/cm³ Show Supplier Material materials with Density of melt of 1450 g/cm³	dry	-
Schrumpfung	0.4 % Show Supplier Material materials with Schrumpfung of 0.4 %	dry	Sim. to ISO 294-4	Parallel
	1.1 % Show Supplier Material materials with Schrumpfung of 1.1 %	dry	Sim. to ISO 294-4	Normal
Specific heat capacity melt	1620 J/(kg·K) Show Supplier Material materials with Specific heat capacity melt of 1620 J/(kg·K)	dry	-
Spiral flow length	105	dry	-	1.0 mm 800 bar
	115	dry	-	1.0 mm 900 bar
	125	dry	-	1.0 mm 1000 bar
	36	dry	-	0.5mm 1200 bar
	50	dry	-	0.5mm 1600 bar
	74	dry	-	0.5mm 2000 bar
Thermal conductivity of melt	0.26 W/(m·K) Show Supplier Material materials with Thermal conductivity of melt of 0.26 W/(m·K)	dry	-
Viscosity number	145 cm³/gr Show Supplier Material materials with Viscosity number of 145 cm³/gr	dry	ISO 307, 1157, 1628

Technological properties

Property
Certifications	Yellow Card Available
Fillers	30% Glass Fiber

Stanyl® TW250F6

Description

Ashby charts

Materialien von diesem Anbieter

Eigenschaften