Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.64 g/cm³ Show Supplier Material materials with Dichte of 1.64 g/cm³ | dry | ISO 1183 |
Moisture absorption | 1.6 % Show Supplier Material materials with Moisture absorption of 1.6 % | dry | Sim. to ISO 62 |
Wasserabsorption | 4.2 % Show Supplier Material materials with Wasserabsorption of 4.2 % | dry | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Thickness | Comment |
|---|---|---|---|---|---|---|
Biegemodul | 16.5 GPa Show Supplier Material materials with Biegemodul of 16.5 GPa | dry | ISO 178 | |||
17.5 GPa Show Supplier Material materials with Biegemodul of 17.5 GPa | conditioned | ISO 178 | ||||
Dehnung | 2.3 % Show Supplier Material materials with Dehnung of 2.3 % | conditioned | ISO 527-1/-2 | |||
2.4 % Show Supplier Material materials with Dehnung of 2.4 % | dry | ISO 527-1/-2 | 1 mm | |||
2.5 % Show Supplier Material materials with Dehnung of 2.5 % | dry | ISO 527-1/-2 | 1 mm | |||
Elastizitätsmodul | 17.5 GPa Show Supplier Material materials with Elastizitätsmodul of 17.5 GPa | dry | ISO 527-1/-2 | 1 mm | ||
17.5 GPa Show Supplier Material materials with Elastizitätsmodul of 17.5 GPa | dry | ISO 527-1/-2 | 1 mm | |||
18.5 GPa Show Supplier Material materials with Elastizitätsmodul of 18.5 GPa | conditioned | ISO 527-1/-2 | ||||
Flexural yield strength | 350 MPa Show Supplier Material materials with Flexural yield strength of 350 MPa | conditioned | ISO 178 | |||
400 MPa Show Supplier Material materials with Flexural yield strength of 400 MPa | dry | ISO 178 | ||||
Schlagfestigkeit, Charpy gekerbt | 23 °C | 12.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 12.5 kJ/m² | conditioned | ISO 179/1eA | ||
23 °C | 14.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14.5 kJ/m² | dry | ISO 179/1eA | |||
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 75 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 75 kJ/m² | conditioned | ISO 179/1eU | ||
23 °C | 90 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 90 kJ/m² | dry | ISO 179/1eU | |||
Zugfestigkeit | 240 MPa Show Supplier Material materials with Zugfestigkeit of 240 MPa | conditioned | ISO 527-1/-2 | |||
270 MPa Show Supplier Material materials with Zugfestigkeit of 270 MPa | dry | ISO 527-1/-2 | 1 mm | at low thickness | ||
280 MPa Show Supplier Material materials with Zugfestigkeit of 280 MPa | dry | ISO 527-1/-2 | 1 mm |
Thermisch
| Property | Value | Condition | Testing Standard | Pressure | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 2e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 5e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
Schmelzpunkt | 315 °C Show Supplier Material materials with Schmelzpunkt of 315 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 245 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 245 °C | dry | ISO 75-1/-2 | 2 MPa |
Elektrisch
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Mobile Phone Mid-Frame | |
| Certifications | Yellow Card Available | |
| Fillers | 50% Glass Fiber | |