Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.06 g/cm³ Show Supplier Material materials with Dichte of 1.06 g/cm³ | dry | ISO 1183 |
Moisture absorption | 2.5 % Show Supplier Material materials with Moisture absorption of 2.5 % | dry | Sim. to ISO 62 |
Wasserabsorption | 7 % Show Supplier Material materials with Wasserabsorption of 7 % | dry | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard |
|---|---|---|---|---|
Biegemodul | 0.5 GPa Show Supplier Material materials with Biegemodul of 0.5 GPa | conditioned | ISO 178 | |
1.7 GPa Show Supplier Material materials with Biegemodul of 1.7 GPa | dry | ISO 178 | ||
Dehnung | -40 °C | 30 % Show Supplier Material materials with Dehnung of 30 % | dry | ISO 527-1/-2 |
50 % Show Supplier Material materials with Dehnung of 50 % | dry, conditioned | ISO 527-1/-2 | ||
Elastizitätsmodul | -40 °C | 2 GPa Show Supplier Material materials with Elastizitätsmodul of 2 GPa | dry | ISO 527-1/-2 |
0.53 GPa Show Supplier Material materials with Elastizitätsmodul of 0.53 GPa | conditioned | ISO 527-1/-2 | ||
1.8 GPa Show Supplier Material materials with Elastizitätsmodul of 1.8 GPa | dry | ISO 527-1/-2 | ||
Elongation at yield | -40 °C | 9 % Show Supplier Material materials with Elongation at yield of 9 % | dry | ISO 527-1/-2 |
4.2 % Show Supplier Material materials with Elongation at yield of 4.2 % | dry | ISO 527-1/-2 | ||
Flexural yield strength | 20 MPa Show Supplier Material materials with Flexural yield strength of 20 MPa | conditioned | ISO 178 | |
63 MPa Show Supplier Material materials with Flexural yield strength of 63 MPa | dry | ISO 178 | ||
Puncture energy | -40 °C | 65 J Show Supplier Material materials with Puncture energy of 65 J | dry | ISO 6603-2 |
23 °C | 48 J Show Supplier Material materials with Puncture energy of 48 J | dry | ISO 6603-2 | |
Puncture force | -40 °C | 5000 N Show Supplier Material materials with Puncture force of 5000 N | dry | ISO 6603-2 |
23 °C | 3300 N Show Supplier Material materials with Puncture force of 3300 N | dry | ISO 6603-2 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | conditioned | ISO 179/1eA |
-30 °C | 22 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 22 kJ/m² | dry | ISO 179/1eA | |
23 °C | 80 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 80 kJ/m² | dry | ISO 179/1eA | |
Streckgrenze | -40 °C | 71 MPa Show Supplier Material materials with Streckgrenze of 71 MPa | dry | ISO 527-1/-2 |
43 MPa Show Supplier Material materials with Streckgrenze of 43 MPa | dry | ISO 527-1/-2 | ||
Zugfestigkeit | -40 °C | 55.0 MPa Show Supplier Material materials with Zugfestigkeit of 55.0 MPa | dry | ISO 527-1/-2 |
37 MPa Show Supplier Material materials with Zugfestigkeit of 37 MPa | dry | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Testing Standard | Pressure | Comment |
|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1e-06 1/K | dry | ISO 11359-1/-2 | Parallel | |
1.1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.1e-06 1/K | dry | ISO 11359-1/-2 | Normal | ||
Temperaturleitfähigkeit | 9.37e-08 mm²/s Show Supplier Material materials with Temperaturleitfähigkeit of 9.37e-08 mm²/s | dry | - | ||
Vicat-Erweichungstemperatur | 130 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 130 °C | dry | ISO 306 | 50°C/h 50N | |
Wärmeformbeständigkeitstemperatur | 55 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 55 °C | dry | ISO 75-1/-2 | 2 MPa | |
100 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 100 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Rheological Properties
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Density of melt | 869 g/cm³ Show Supplier Material materials with Density of melt of 869 g/cm³ | dry | - | ||
Schmelzvolumenflussrate | 250 °C | 13 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 13 cm³/10min | dry | ISO 1133 | |
Schrumpfung | 1.8 % Show Supplier Material materials with Schrumpfung of 1.8 % | dry | ISO 294-4 | Normal | |
1.9 % Show Supplier Material materials with Schrumpfung of 1.9 % | dry | ISO 294-4 | Parallel | ||
Specific heat capacity melt | 2740 J/(kg·K) Show Supplier Material materials with Specific heat capacity melt of 2740 J/(kg·K) | dry | - | ||
Thermal conductivity of melt | 0.22 W/(m·K) Show Supplier Material materials with Thermal conductivity of melt of 0.22 W/(m·K) | dry | - |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Outdoor power product fuel tanks, High pressure type IV composite fuel tanks | |