Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.37 g/cm³ Show Supplier Material materials with Dichte of 1.37 g/cm³ | dry | ISO 1183 |
Moisture absorption | 1.7 % Show Supplier Material materials with Moisture absorption of 1.7 % | dry | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard |
|---|---|---|---|---|
Biegemodul | 6.5 GPa Show Supplier Material materials with Biegemodul of 6.5 GPa | conditioned | ISO 178 | |
8.3 GPa Show Supplier Material materials with Biegemodul of 8.3 GPa | dry | ISO 178 | ||
Dehnung | 2.6 % Show Supplier Material materials with Dehnung of 2.6 % | dry | ISO 527-1/-2 | |
4 % Show Supplier Material materials with Dehnung of 4 % | conditioned | ISO 527-1/-2 | ||
Elastizitätsmodul | 6.5 GPa Show Supplier Material materials with Elastizitätsmodul of 6.5 GPa | conditioned | ISO 527-1/-2 | |
9.7 GPa Show Supplier Material materials with Elastizitätsmodul of 9.7 GPa | dry | ISO 527-1/-2 | ||
Flexural yield strength | 200 MPa Show Supplier Material materials with Flexural yield strength of 200 MPa | conditioned | ISO 178 | |
265 MPa Show Supplier Material materials with Flexural yield strength of 265 MPa | dry | ISO 178 | ||
Schlagfestigkeit, Charpy gekerbt | 23 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | dry | ISO 179/1eA |
23 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | conditioned | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | 23 °C | 80 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | conditioned | ISO 179/1eU |
23 °C | 110 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 110 kJ/m² | dry | ISO 179/1eU | |
Zugfestigkeit | 130 MPa Show Supplier Material materials with Zugfestigkeit of 130 MPa | conditioned | ISO 527-1/-2 | |
170 MPa Show Supplier Material materials with Zugfestigkeit of 170 MPa | dry | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Thickness | Testing Standard | Pressure | Comment |
|---|---|---|---|---|---|---|
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | dry | 0.75 mm | UL746B | ||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | dry | 0.75 mm | UL746B | ||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | dry | 0.75 mm | UL746B | ||
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | dry | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 244 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 244 °C | dry | ISO 75-1/-2 | 2 MPa | ||
260 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 260 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Dielektrizitätskonstante | 4 [-] Show Supplier Material materials with Dielektrizitätskonstante of 4 [-] | dry | IEC 62631-2-1 | 1MHz |
Durchschlagfestigkeit | 26 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 26 kV/mm | dry | IEC 60243-1 | |
Kriechstromfestigkeit | 550 V Show Supplier Material materials with Kriechstromfestigkeit of 550 V | dry | IEC 60112 | |
Surface resistivity | 4e+14 Ω/sq Show Supplier Material materials with Surface resistivity of 4e+14 Ω/sq | conditioned | IEC 62631-3-2 | |
Verlustfaktor | 190 [-] Show Supplier Material materials with Verlustfaktor of 190 [-] | dry | IEC 62631-2-1 | 1MHz |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Schmelzmassenflussrate | 280 °C | 15 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 15 g/10min | dry | ISO 1133 | |
Schmelzvolumenflussrate | 280 °C | 12 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 12 cm³/10min | dry | ISO 1133 | |
Schrumpfung | 0.4 % Show Supplier Material materials with Schrumpfung of 0.4 % | dry | Sim. to ISO 294-4 | Parallel | |
1.3 % Show Supplier Material materials with Schrumpfung of 1.3 % | dry | Sim. to ISO 294-4 | Normal |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 30% Glass Fiber | |