| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Dichte | 1.22 g/cm³ Show Supplier Material materials with Dichte of 1.22 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 0.5 % Show Supplier Material materials with Moisture absorption of 0.5 % | dry | Sim. to ISO 62 | |
Wasserabsorption | 2.2 % Show Supplier Material materials with Wasserabsorption of 2.2 % | dry | ISO 62 | at 23°C after 24h |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Biegemodul | 0.2 GPa Show Supplier Material materials with Biegemodul of 0.2 GPa | dry | ISO 178 | ||
120 °C | 0.07 GPa Show Supplier Material materials with Biegemodul of 0.07 GPa | dry | ISO 178 | ||
Dehnung | 150 % Show Supplier Material materials with Dehnung of 150 % | dry | ISO 527-1/-2 | ||
640 % Show Supplier Material materials with Dehnung of 640 % | dry | ISO 527-1/-2 | |||
Elastizitätsmodul | 0.17 GPa Show Supplier Material materials with Elastizitätsmodul of 0.17 GPa | dry | ISO 527-1/-2 | ||
Härte, Shore A | 94 [-] Show Supplier Material materials with Härte, Shore A of 94 [-] | dry | ISO 868 | 3s | |
Härte, Shore D | 50 [-] Show Supplier Material materials with Härte, Shore D of 50 [-] | dry | ISO 868 | 3s | |
Reißfestigkeit | 116 kN/m Show Supplier Material materials with Reißfestigkeit of 116 kN/m | dry | ISO 34-1; Method B | ||
121 kN/m Show Supplier Material materials with Reißfestigkeit of 121 kN/m | dry | ISO 34-1; Method B | |||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 14.0 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14.0 kJ/m² | dry | ISO 179/1eA | |
Zugfestigkeit | 27 MPa Show Supplier Material materials with Zugfestigkeit of 27 MPa | dry | ISO 527-1/-2 | ||
36 MPa Show Supplier Material materials with Zugfestigkeit of 36 MPa | dry | ISO 527-1/-2 | Normal |
Thermisch
| Property | Value | Condition | Testing Standard | Pressure | Comment |
|---|---|---|---|---|---|
Glasübergangstemperatur | -57.0 °C Show Supplier Material materials with Glasübergangstemperatur of -57.0 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Schmelzpunkt | 202 °C Show Supplier Material materials with Schmelzpunkt of 202 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 63 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 63 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Rheological Properties
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Schmelzvolumenflussrate | 230 °C | 2 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 2 cm³/10min | dry | ISO 1133 | |
Schrumpfung | 1.7 % Show Supplier Material materials with Schrumpfung of 1.7 % | dry | ISO 294-4 | Parallel | |
1.8 % Show Supplier Material materials with Schrumpfung of 1.8 % | dry | ISO 294-4 | Normal |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Clean Air Inlet Ducts, Cold Charged Air Ducts | |