Allgemein
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dichte | 1.37 g/cm³ Show Supplier Material materials with Dichte of 1.37 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 2.4 % Show Supplier Material materials with Moisture absorption of 2.4 % | dry | Sim. to ISO 62 | |
Wasserabsorption | 3 % Show Supplier Material materials with Wasserabsorption of 3 % | dry | ISO 62 | at 23°C after 24h |
6.9 % Show Supplier Material materials with Wasserabsorption of 6.9 % | dry | Sim. to ISO 62 |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Biegemodul | 9.4 GPa Show Supplier Material materials with Biegemodul of 9.4 GPa | dry | ISO 178 | |
120 °C | 4 GPa Show Supplier Material materials with Biegemodul of 4 GPa | dry | ISO 178 | |
160 °C | 3.7 GPa Show Supplier Material materials with Biegemodul of 3.7 GPa | dry | ISO 178 | |
180 °C | 3.4 GPa Show Supplier Material materials with Biegemodul of 3.4 GPa | dry | ISO 178 | |
200 °C | 3.1 GPa Show Supplier Material materials with Biegemodul of 3.1 GPa | dry | ISO 178 | |
210 °C | 2.9 GPa Show Supplier Material materials with Biegemodul of 2.9 GPa | dry | ISO 178 | |
Dehnung | -40 °C | 3.2 % Show Supplier Material materials with Dehnung of 3.2 % | dry | ISO 527-1/-2 |
3.3 % Show Supplier Material materials with Dehnung of 3.3 % | dry | ISO 527-1/-2 | ||
6.5 % Show Supplier Material materials with Dehnung of 6.5 % | conditioned | ISO 527-1/-2 | ||
120 °C | 10 % Show Supplier Material materials with Dehnung of 10 % | dry | ISO 527-1/-2 | |
150 °C | 10.6 % Show Supplier Material materials with Dehnung of 10.6 % | dry | ISO 527-1/-2 | |
160 °C | 10.8 % Show Supplier Material materials with Dehnung of 10.8 % | dry | ISO 527-1/-2 | |
180 °C | 11.1 % Show Supplier Material materials with Dehnung of 11.1 % | dry | ISO 527-1/-2 | |
200 °C | 11.5 % Show Supplier Material materials with Dehnung of 11.5 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | -40 °C | 10 GPa Show Supplier Material materials with Elastizitätsmodul of 10 GPa | dry | ISO 527-1/-2 |
5.5 GPa Show Supplier Material materials with Elastizitätsmodul of 5.5 GPa | conditioned | ISO 527-1/-2 | ||
9.8 GPa Show Supplier Material materials with Elastizitätsmodul of 9.8 GPa | dry | ISO 527-1/-2 | ||
40 °C | 9.3 GPa Show Supplier Material materials with Elastizitätsmodul of 9.3 GPa | dry | ISO 527-1/-2 | |
120 °C | 4.2 GPa Show Supplier Material materials with Elastizitätsmodul of 4.2 GPa | dry | ISO 527-1/-2 | |
150 °C | 3.9 GPa Show Supplier Material materials with Elastizitätsmodul of 3.9 GPa | dry | ISO 527-1/-2 | |
160 °C | 3.3 GPa Show Supplier Material materials with Elastizitätsmodul of 3.3 GPa | dry | ISO 527-1/-2 | |
180 °C | 3.0 GPa Show Supplier Material materials with Elastizitätsmodul of 3.0 GPa | dry | ISO 527-1/-2 | |
200 °C | 2.6 GPa Show Supplier Material materials with Elastizitätsmodul of 2.6 GPa | dry | ISO 527-1/-2 | |
210 °C | 2.4 GPa Show Supplier Material materials with Elastizitätsmodul of 2.4 GPa | dry | ISO 527-1/-2 | |
Flexural yield strength | 280 MPa Show Supplier Material materials with Flexural yield strength of 280 MPa | dry | ISO 178 | |
120 °C | 115 MPa Show Supplier Material materials with Flexural yield strength of 115 MPa | dry | ISO 178 | |
160 °C | 97 MPa Show Supplier Material materials with Flexural yield strength of 97 MPa | dry | ISO 178 | |
180 °C | 87 MPa Show Supplier Material materials with Flexural yield strength of 87 MPa | dry | ISO 178 | |
200 °C | 71 MPa Show Supplier Material materials with Flexural yield strength of 71 MPa | dry | ISO 178 | |
210 °C | 65 MPa Show Supplier Material materials with Flexural yield strength of 65 MPa | dry | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | dry | ISO 179/1eA |
-30 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | conditioned | ISO 179/1eA | |
23 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | dry | ISO 179/1eA | |
23 °C | 22 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 22 kJ/m² | conditioned | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 55.0 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 55.0 kJ/m² | dry, conditioned | ISO 179/1eU |
23 °C | 75 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 75 kJ/m² | dry | ISO 179/1eU | |
23 °C | 85 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 85 kJ/m² | conditioned | ISO 179/1eU | |
Zugfestigkeit | -40 °C | 250 MPa Show Supplier Material materials with Zugfestigkeit of 250 MPa | dry | ISO 527-1/-2 |
95 MPa Show Supplier Material materials with Zugfestigkeit of 95 MPa | conditioned | ISO 527-1/-2 | ||
190 MPa Show Supplier Material materials with Zugfestigkeit of 190 MPa | dry | ISO 527-1/-2 | ||
100 °C | 97 MPa Show Supplier Material materials with Zugfestigkeit of 97 MPa | dry | ISO 527-1/-2 | |
120 °C | 90 MPa Show Supplier Material materials with Zugfestigkeit of 90 MPa | dry | ISO 527-1/-2 | |
150 °C | 77 MPa Show Supplier Material materials with Zugfestigkeit of 77 MPa | dry | ISO 527-1/-2 | |
160 °C | 73 MPa Show Supplier Material materials with Zugfestigkeit of 73 MPa | dry | ISO 527-1/-2 | |
180 °C | 65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | dry | ISO 527-1/-2 | |
200 °C | 55.0 MPa Show Supplier Material materials with Zugfestigkeit of 55.0 MPa | dry | ISO 527-1/-2 | |
210 °C | 50 MPa Show Supplier Material materials with Zugfestigkeit of 50 MPa | dry | ISO 527-1/-2 |
Thermisch
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Schmelzpunkt | 260 °C Show Supplier Material materials with Schmelzpunkt of 260 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 235 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 235 °C | dry | ISO 75-1/-2 | 2 MPa | |
255 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 255 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Integrated Air Inlet Manifolds (up to 230°C), Integrated Air Inlet Manifolds (up to 180°C), Resonators and ByPass Valves, Hot Charged Air Ducts, Charge Air Cooler Caps | |
Fillers | 30% Glass Fiber |