Property | Value | Condition | Testing Standard |
---|---|---|---|
Dichte | 1.14 g/cm³ Show Supplier Material materials with Dichte of 1.14 g/cm³ | dry | ISO 1183 |
Moisture absorption | 3.7 % Show Supplier Material materials with Moisture absorption of 3.7 % | dry | Sim. to ISO 62 |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Biegemodul | 0.65 GPa Show Supplier Material materials with Biegemodul of 0.65 GPa | conditioned | ISO 178 | |
2.4 GPa Show Supplier Material materials with Biegemodul of 2.4 GPa | dry | ISO 178 | ||
80 °C | 0.8 GPa Show Supplier Material materials with Biegemodul of 0.8 GPa | dry | ISO 178 | |
Dehnung | 35 % Show Supplier Material materials with Dehnung of 35 % | dry | ISO 527-1/-2 | |
120 °C | 50 % Show Supplier Material materials with Dehnung of 50 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | 0.7 GPa Show Supplier Material materials with Elastizitätsmodul of 0.7 GPa | conditioned | ISO 527-1/-2 | |
2.5 GPa Show Supplier Material materials with Elastizitätsmodul of 2.5 GPa | dry | ISO 527-1/-2 | ||
120 °C | 0.56 GPa Show Supplier Material materials with Elastizitätsmodul of 0.56 GPa | dry | ISO 527-1/-2 | |
Elongation at yield | 18 % Show Supplier Material materials with Elongation at yield of 18 % | dry | ISO 527-1/-2 | |
30 % Show Supplier Material materials with Elongation at yield of 30 % | conditioned | ISO 527-1/-2 | ||
Flexural yield strength | 19 MPa Show Supplier Material materials with Flexural yield strength of 19 MPa | conditioned | ISO 178 | |
93 MPa Show Supplier Material materials with Flexural yield strength of 93 MPa | dry | ISO 178 | ||
80 °C | 33 MPa Show Supplier Material materials with Flexural yield strength of 33 MPa | dry | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 14.0 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14.0 kJ/m² | dry | ISO 179/1eA |
-30 °C | 16 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 16 kJ/m² | conditioned | ISO 179/1eA | |
23 °C | 22 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 22 kJ/m² | dry | ISO 179/1eA | |
23 °C | 130 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 130 kJ/m² | conditioned | ISO 179/1eA | |
Streckgrenze | 40 MPa Show Supplier Material materials with Streckgrenze of 40 MPa | conditioned | ISO 527-1/-2 | |
75 MPa Show Supplier Material materials with Streckgrenze of 75 MPa | dry | ISO 527-1/-2 | ||
120 °C | 35 MPa Show Supplier Material materials with Streckgrenze of 35 MPa | dry | ISO 527-1/-2 | |
Zugfestigkeit | 65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | dry | ISO 527-1/-2 | |
120 °C | 45 MPa Show Supplier Material materials with Zugfestigkeit of 45 MPa | dry | ISO 527-1/-2 |
Thermisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Glasübergangstemperatur | 75 °C Show Supplier Material materials with Glasübergangstemperatur of 75 °C | dry | ISO 11357-1/-2 | 10°C/min |
Koeffizient der thermischen Ausdehnung | 9e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9e-07 1/K | dry | ISO 11359-1/-2 | Parallel |
1.1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.1e-06 1/K | dry | ISO 11359-1/-2 | Normal | |
Schmelzpunkt | 295 °C Show Supplier Material materials with Schmelzpunkt of 295 °C | dry | ISO 11357-1/-3 | 10°C/min |
Temperaturleitfähigkeit | 9.82e-07 mm²/s Show Supplier Material materials with Temperaturleitfähigkeit of 9.82e-07 mm²/s | dry | - |
Rheological Properties
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Density of melt | 913 g/cm³ Show Supplier Material materials with Density of melt of 913 g/cm³ | dry | - | |
Schrumpfung | 2 % Show Supplier Material materials with Schrumpfung of 2 % | dry | Sim. to ISO 294-4 | Parallel |
2 % Show Supplier Material materials with Schrumpfung of 2 % | dry | Sim. to ISO 294-4 | Normal | |
Specific heat capacity melt | 2550 J/(kg·K) Show Supplier Material materials with Specific heat capacity melt of 2550 J/(kg·K) | dry | - | |
Thermal conductivity of melt | 0.24 W/(m·K) Show Supplier Material materials with Thermal conductivity of melt of 0.24 W/(m·K) | dry | - |
Technological properties
Property | ||
---|---|---|
Application areas | Timing drive systems |