Property | Value | Condition | Testing Standard |
---|---|---|---|
Dichte | 1.02 g/cm³ Show Supplier Material materials with Dichte of 1.02 g/cm³ | dry | ISO 1183 |
Moisture absorption | 1.8 % Show Supplier Material materials with Moisture absorption of 1.8 % | dry | Sim. to ISO 62 |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Biegemodul | 0.42 GPa Show Supplier Material materials with Biegemodul of 0.42 GPa | conditioned | ISO 178 | |
1.1 GPa Show Supplier Material materials with Biegemodul of 1.1 GPa | dry | ISO 178 | ||
Dehnung | 50 % Show Supplier Material materials with Dehnung of 50 % | dry, conditioned | ISO 527-1/-2 | |
Elastizitätsmodul | 0.4 GPa Show Supplier Material materials with Elastizitätsmodul of 0.4 GPa | conditioned | ISO 527-1/-2 | |
1 GPa Show Supplier Material materials with Elastizitätsmodul of 1 GPa | dry | ISO 527-1/-2 | ||
Elongation at yield | 4.4 % Show Supplier Material materials with Elongation at yield of 4.4 % | dry | ISO 527-1/-2 | |
20 % Show Supplier Material materials with Elongation at yield of 20 % | conditioned | ISO 527-1/-2 | ||
Flexural yield strength | 20 MPa Show Supplier Material materials with Flexural yield strength of 20 MPa | conditioned | ISO 178 | |
39 MPa Show Supplier Material materials with Flexural yield strength of 39 MPa | dry | ISO 178 | ||
Schlagfestigkeit, Charpy gekerbt | 23 °C | 100 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 100 kJ/m² | dry | ISO 179/1eA |
Thermisch
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1e-06 1/K | dry | ISO 11359-1/-2 | Parallel | |
1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1e-06 1/K | dry | ISO 11359-1/-2 | Normal | ||
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 50 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 50 °C | dry | ISO 75-1/-2 | 2 MPa | |
62 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 62 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dielektrizitätskonstante | 3 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3 [-] | dry | IEC 62631-2-1 | 100Hz |
3 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3 [-] | dry | IEC 62631-2-1 | 1MHz | |
Durchschlagfestigkeit | 33 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 33 kV/mm | dry | IEC 60243-1 | |
Kriechstromfestigkeit | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | dry | IEC 60112 | |
Surface resistivity | 2e+13 Ω/sq Show Supplier Material materials with Surface resistivity of 2e+13 Ω/sq | conditioned | IEC 62631-3-2 | |
Verlustfaktor | 100 [-] Show Supplier Material materials with Verlustfaktor of 100 [-] | dry | IEC 62631-2-1 | 100Hz |
130 [-] Show Supplier Material materials with Verlustfaktor of 130 [-] | dry | IEC 62631-2-1 | 1MHz | |
Volume resistivity | 9e+12 Ω·cm Show Supplier Material materials with Volume resistivity of 9e+12 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
Property | Temperature | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|---|
Schmelzmassenflussrate | 230 °C | 1 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 1 g/10min | dry | ISO 1133 | |
Schmelzvolumenflussrate | 230 °C | 1 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 1 cm³/10min | dry | ISO 1133 | |
Schrumpfung | 1.8 % Show Supplier Material materials with Schrumpfung of 1.8 % | dry | Sim. to ISO 294-4 | Parallel | |
2.2 % Show Supplier Material materials with Schrumpfung of 2.2 % | dry | Sim. to ISO 294-4 | Normal |
Technological properties
Property |
---|