Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Dichte | 1.63 g/cm³ Show Supplier Material materials with Dichte of 1.63 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 1.8 % Show Supplier Material materials with Moisture absorption of 1.8 % | dry | Sim. to ISO 62 | |
Wasserabsorption | 1.9 % Show Supplier Material materials with Wasserabsorption of 1.9 % | dry | ISO 62 | at 23°C after 24h |
6.75 % Show Supplier Material materials with Wasserabsorption of 6.75 % | dry | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard |
|---|---|---|---|---|
Biegemodul | 11 GPa Show Supplier Material materials with Biegemodul of 11 GPa | dry | ISO 178 | |
Dehnung | 2 % Show Supplier Material materials with Dehnung of 2 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | 14.5 GPa Show Supplier Material materials with Elastizitätsmodul of 14.5 GPa | dry | ISO 527-1/-2 | |
Flexural yield strength | 225 MPa Show Supplier Material materials with Flexural yield strength of 225 MPa | dry | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 4.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 4.5 kJ/m² | dry | ISO 179/1eA |
23 °C | 6 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | dry | ISO 179/1eA | |
Zugfestigkeit | 160 MPa Show Supplier Material materials with Zugfestigkeit of 160 MPa | dry | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Testing Standard | Pressure | Comment |
|---|---|---|---|---|---|
Glasübergangstemperatur | 75 °C Show Supplier Material materials with Glasübergangstemperatur of 75 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Koeffizient der thermischen Ausdehnung | 2.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 2.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 5e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
Schmelzpunkt | 295 °C Show Supplier Material materials with Schmelzpunkt of 295 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Temperaturleitfähigkeit | 1.64e-07 mm²/s Show Supplier Material materials with Temperaturleitfähigkeit of 1.64e-07 mm²/s | dry | - | ||
Wärmeformbeständigkeitstemperatur | 285 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 285 °C | dry | ISO 75-1/-2 | 2 MPa | |
290 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 290 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Density of melt | 1430.0 g/cm³ Show Supplier Material materials with Density of melt of 1430.0 g/cm³ | dry | - | |
Schrumpfung | 0.2 % Show Supplier Material materials with Schrumpfung of 0.2 % | dry | Sim. to ISO 294-4 | Parallel |
1.25 % Show Supplier Material materials with Schrumpfung of 1.25 % | dry | Sim. to ISO 294-4 | Normal | |
Specific heat capacity melt | 1680 J/(kg·K) Show Supplier Material materials with Specific heat capacity melt of 1680 J/(kg·K) | dry | - | |
Spiral flow length | 32 | dry | - | 0.5mm 1200 bar |
48 | dry | - | 0.5mm 1600 bar | |
60 | dry | - | 0.5mm 2000 bar | |
Thermal conductivity of melt | 0.391 W/(m·K) Show Supplier Material materials with Thermal conductivity of melt of 0.391 W/(m·K) | dry | - |
Technological properties
| Property | ||
|---|---|---|
| Fillers | 50% Glass Fiber and Mineral Fiber | |