Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Dichte | 1.74 g/cm³ Show Supplier Material materials with Dichte of 1.74 g/cm³ | dry | ISO 1183 | |
Moisture absorption | 0.04 % Show Supplier Material materials with Moisture absorption of 0.04 % | dry | Sim. to ISO 62 | |
Wasserabsorption | 0.04 % Show Supplier Material materials with Wasserabsorption of 0.04 % | dry | ISO 62 | at 23°C after 24h |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard |
|---|---|---|---|---|
Biegemodul | 14.5 GPa Show Supplier Material materials with Biegemodul of 14.5 GPa | dry | ISO 178 | |
120 °C | 7.2 GPa Show Supplier Material materials with Biegemodul of 7.2 GPa | dry | ISO 178 | |
160 °C | 5.5 GPa Show Supplier Material materials with Biegemodul of 5.5 GPa | dry | ISO 178 | |
200 °C | 4.8 GPa Show Supplier Material materials with Biegemodul of 4.8 GPa | dry | ISO 178 | |
Dehnung | -40 °C | 2.2 % Show Supplier Material materials with Dehnung of 2.2 % | dry | ISO 527-1/-2 |
2 % Show Supplier Material materials with Dehnung of 2 % | dry | ISO 527-1/-2 | ||
120 °C | 3.5 % Show Supplier Material materials with Dehnung of 3.5 % | dry | ISO 527-1/-2 | |
160 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | -40 °C | 15.5 GPa Show Supplier Material materials with Elastizitätsmodul of 15.5 GPa | dry | ISO 527-1/-2 |
15 GPa Show Supplier Material materials with Elastizitätsmodul of 15 GPa | dry | ISO 527-1/-2 | ||
120 °C | 7.5 GPa Show Supplier Material materials with Elastizitätsmodul of 7.5 GPa | dry | ISO 527-1/-2 | |
160 °C | 5.5 GPa Show Supplier Material materials with Elastizitätsmodul of 5.5 GPa | dry | ISO 527-1/-2 | |
Flexural yield strength | 280 MPa Show Supplier Material materials with Flexural yield strength of 280 MPa | dry | ISO 178 | |
120 °C | 138 MPa Show Supplier Material materials with Flexural yield strength of 138 MPa | dry | ISO 178 | |
160 °C | 100 MPa Show Supplier Material materials with Flexural yield strength of 100 MPa | dry | ISO 178 | |
200 °C | 80 MPa Show Supplier Material materials with Flexural yield strength of 80 MPa | dry | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | dry | ISO 179/1eA |
23 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 60 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 60 kJ/m² | dry | ISO 179/1eU |
23 °C | 55.0 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 55.0 kJ/m² | dry | ISO 179/1eU | |
Zugfestigkeit | -40 °C | 245 MPa Show Supplier Material materials with Zugfestigkeit of 245 MPa | dry | ISO 527-1/-2 |
200 MPa Show Supplier Material materials with Zugfestigkeit of 200 MPa | dry | ISO 527-1/-2 | ||
120 °C | 86 MPa Show Supplier Material materials with Zugfestigkeit of 86 MPa | dry | ISO 527-1/-2 | |
160 °C | 65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | dry | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Thickness | Testing Standard | Pressure | Comment |
|---|---|---|---|---|---|---|
Entflammbarkeit | V-0 | dry | 1.5 mm | IEC 60695-11-10 | UL recognition :Yes | |
Glasübergangstemperatur | 90 °C Show Supplier Material materials with Glasübergangstemperatur of 90 °C | dry | ISO 11357-1/-2 | 10°C/min | ||
Koeffizient der thermischen Ausdehnung | 1.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | ||
1.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.5e-07 1/K | dry | ISO 11359-1/-2 | parallel, above Tg | |||
4e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4e-07 1/K | dry | ISO 11359-1/-2 | Normal | |||
1.1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.1e-06 1/K | dry | ISO 11359-1/-2 | normal, above Tg | |||
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | dry | 0.4 mm | UL746B | ||
Relative temperature index, mechanical impact | 130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C | dry | 0.4 mm | UL746B | ||
Relative temperature index, mechanical strength | 130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C | dry | 0.4 mm | UL746B | ||
Schmelzpunkt | 280 °C Show Supplier Material materials with Schmelzpunkt of 280 °C | dry | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 265 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 265 °C | dry | ISO 75-1/-2 | 2 MPa |
Elektrisch
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Kriechstromfestigkeit | 175 V Show Supplier Material materials with Kriechstromfestigkeit of 175 V | dry | IEC 60112 |
Surface resistivity | 1e+15 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq | dry | IEC 62631-3-2 |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Fillers | 40% Glass Fiber | |