Property | Value | Condition | Testing Standard |
---|---|---|---|
Dichte | 1.79 g/cm³ Show Supplier Material materials with Dichte of 1.79 g/cm³ | dry | ISO 1183 |
Wasserabsorption | 2.5 % Show Supplier Material materials with Wasserabsorption of 2.5 % | dry | Sim. to ISO 62 |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Biegemodul | 23 GPa Show Supplier Material materials with Biegemodul of 23 GPa | dry | ISO 178 | |
120 °C | 20 GPa Show Supplier Material materials with Biegemodul of 20 GPa | dry | ISO 178 | |
160 °C | 1.1 GPa Show Supplier Material materials with Biegemodul of 1.1 GPa | dry | ISO 178 | |
180 °C | 9 GPa Show Supplier Material materials with Biegemodul of 9 GPa | dry | ISO 178 | |
200 °C | 8 GPa Show Supplier Material materials with Biegemodul of 8 GPa | dry | ISO 178 | |
Dehnung | -40 °C | 1.8 % Show Supplier Material materials with Dehnung of 1.8 % | dry | ISO 527-1/-2 |
1.8 % Show Supplier Material materials with Dehnung of 1.8 % | dry | ISO 527-1/-2 | ||
40 °C | 1.8 % Show Supplier Material materials with Dehnung of 1.8 % | dry | ISO 527-1/-2 | |
80 °C | 1.8 % Show Supplier Material materials with Dehnung of 1.8 % | dry | ISO 527-1/-2 | |
100 °C | 1.8 % Show Supplier Material materials with Dehnung of 1.8 % | dry | ISO 527-1/-2 | |
120 °C | 1.9 % Show Supplier Material materials with Dehnung of 1.9 % | dry | ISO 527-1/-2 | |
150 °C | 3.5 % Show Supplier Material materials with Dehnung of 3.5 % | dry | ISO 527-1/-2 | |
160 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | dry | ISO 527-1/-2 | |
180 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | dry | ISO 527-1/-2 | |
200 °C | 4 % Show Supplier Material materials with Dehnung of 4 % | dry | ISO 527-1/-2 | |
210 °C | 0.004 % Show Supplier Material materials with Dehnung of 0.004 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | -40 °C | 25 GPa Show Supplier Material materials with Elastizitätsmodul of 25 GPa | dry | ISO 527-1/-2 |
23 GPa Show Supplier Material materials with Elastizitätsmodul of 23 GPa | dry | ISO 527-1/-2 | ||
40 °C | 22.5 GPa Show Supplier Material materials with Elastizitätsmodul of 22.5 GPa | dry | ISO 527-1/-2 | |
80 °C | 22 GPa Show Supplier Material materials with Elastizitätsmodul of 22 GPa | dry | ISO 527-1/-2 | |
100 °C | 21.5 GPa Show Supplier Material materials with Elastizitätsmodul of 21.5 GPa | dry | ISO 527-1/-2 | |
120 °C | 20.5 GPa Show Supplier Material materials with Elastizitätsmodul of 20.5 GPa | dry | ISO 527-1/-2 | |
150 °C | 12.5 GPa Show Supplier Material materials with Elastizitätsmodul of 12.5 GPa | dry | ISO 527-1/-2 | |
160 °C | 9.8 GPa Show Supplier Material materials with Elastizitätsmodul of 9.8 GPa | dry | ISO 527-1/-2 | |
180 °C | 8.1 GPa Show Supplier Material materials with Elastizitätsmodul of 8.1 GPa | dry | ISO 527-1/-2 | |
200 °C | 7.4 GPa Show Supplier Material materials with Elastizitätsmodul of 7.4 GPa | dry | ISO 527-1/-2 | |
210 °C | 7 GPa Show Supplier Material materials with Elastizitätsmodul of 7 GPa | dry | ISO 527-1/-2 | |
Flexural yield strength | 420 MPa Show Supplier Material materials with Flexural yield strength of 420 MPa | dry | ISO 178 | |
120 °C | 270 MPa Show Supplier Material materials with Flexural yield strength of 270 MPa | dry | ISO 178 | |
160 °C | 150 MPa Show Supplier Material materials with Flexural yield strength of 150 MPa | dry | ISO 178 | |
180 °C | 120 MPa Show Supplier Material materials with Flexural yield strength of 120 MPa | dry | ISO 178 | |
200 °C | 105 MPa Show Supplier Material materials with Flexural yield strength of 105 MPa | dry | ISO 178 | |
210 °C | 100 MPa Show Supplier Material materials with Flexural yield strength of 100 MPa | dry | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | dry | ISO 179/1eA |
23 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 80 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 80 kJ/m² | dry | ISO 179/1eU |
23 °C | 90 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 90 kJ/m² | dry | ISO 179/1eU | |
Zugfestigkeit | -40 °C | 330 MPa Show Supplier Material materials with Zugfestigkeit of 330 MPa | dry | ISO 527-1/-2 |
270 MPa Show Supplier Material materials with Zugfestigkeit of 270 MPa | dry | ISO 527-1/-2 | ||
40 °C | 260 MPa Show Supplier Material materials with Zugfestigkeit of 260 MPa | dry | ISO 527-1/-2 | |
80 °C | 230 MPa Show Supplier Material materials with Zugfestigkeit of 230 MPa | dry | ISO 527-1/-2 | |
100 °C | 210 MPa Show Supplier Material materials with Zugfestigkeit of 210 MPa | dry | ISO 527-1/-2 | |
120 °C | 180 MPa Show Supplier Material materials with Zugfestigkeit of 180 MPa | dry | ISO 527-1/-2 | |
150 °C | 115 MPa Show Supplier Material materials with Zugfestigkeit of 115 MPa | dry | ISO 527-1/-2 | |
160 °C | 95 MPa Show Supplier Material materials with Zugfestigkeit of 95 MPa | dry | ISO 527-1/-2 | |
180 °C | 75 MPa Show Supplier Material materials with Zugfestigkeit of 75 MPa | dry | ISO 527-1/-2 | |
200 °C | 65 MPa Show Supplier Material materials with Zugfestigkeit of 65 MPa | dry | ISO 527-1/-2 | |
210 °C | 60 MPa Show Supplier Material materials with Zugfestigkeit of 60 MPa | dry | ISO 527-1/-2 |
Thermisch
Property | Value | Condition | Testing Standard | Thickness | Pressure | Comment |
---|---|---|---|---|---|---|
Glasübergangstemperatur | 155 °C Show Supplier Material materials with Glasübergangstemperatur of 155 °C | dry | ASTM D5026/D7028 | DMTA (tan d) | ||
Glow Wire Flammability Index | 725 °C Show Supplier Material materials with Glow Wire Flammability Index of 725 °C | dry | IEC 60695-2-12 | 2 mm | ||
960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | dry | IEC 60695-2-12 | 3 mm | |||
Glow Wire Ignition Temperature | 725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | dry | IEC 60695-2-13 | 2 mm | ||
850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | dry | IEC 60695-2-13 | 3 mm | |||
Koeffizient der thermischen Ausdehnung | 1.3e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.3e-07 1/K | dry | ISO 11359-1/-2 | Parallel | ||
4.1e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.1e-07 1/K | dry | ISO 11359-1/-2 | Normal | |||
Schmelzpunkt | 330 °C Show Supplier Material materials with Schmelzpunkt of 330 °C | dry | ISO 11357-1/-3 | 10°C/min | ||
Wärmeformbeständigkeitstemperatur | 307 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 307 °C | dry | ISO 75-1/-2 | 2 MPa | ||
320 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 320 °C | dry | ISO 75-1/-2 | 0.45 MPa |
Elektrisch
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Structural Parts with ForTii® Ace, Timing drive systems | |
Fillers | 60% Glass Fiber |