Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dichte | 1.86 g/cm³ Show Supplier Material materials with Dichte of 1.86 g/cm³ | dry | ISO 1183 | |
Wasserabsorption | 0.04 % Show Supplier Material materials with Wasserabsorption of 0.04 % | dry | ISO 62 | at 23°C after 24h |
Mechanisch
Property | Temperature | Value | Condition | Testing Standard |
---|---|---|---|---|
Biegemodul | 18 GPa Show Supplier Material materials with Biegemodul of 18 GPa | dry | ISO 178 | |
120 °C | 10 GPa Show Supplier Material materials with Biegemodul of 10 GPa | dry | ISO 178 | |
160 °C | 8 GPa Show Supplier Material materials with Biegemodul of 8 GPa | dry | ISO 178 | |
Dehnung | -40 °C | 1.3 % Show Supplier Material materials with Dehnung of 1.3 % | dry | ISO 527-1/-2 |
1.3 % Show Supplier Material materials with Dehnung of 1.3 % | dry | ISO 527-1/-2 | ||
120 °C | 2.2 % Show Supplier Material materials with Dehnung of 2.2 % | dry | ISO 527-1/-2 | |
160 °C | 2.3 % Show Supplier Material materials with Dehnung of 2.3 % | dry | ISO 527-1/-2 | |
Elastizitätsmodul | 19 GPa Show Supplier Material materials with Elastizitätsmodul of 19 GPa | dry | ISO 527-1/-2 | |
Flexural yield strength | 280 MPa Show Supplier Material materials with Flexural yield strength of 280 MPa | dry | ISO 178 | |
120 °C | 160 MPa Show Supplier Material materials with Flexural yield strength of 160 MPa | dry | ISO 178 | |
160 °C | 120 MPa Show Supplier Material materials with Flexural yield strength of 120 MPa | dry | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 9.8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 9.8 kJ/m² | dry | ISO 179/1eA |
23 °C | 8.8 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 8.8 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 40 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 40 kJ/m² | dry | ISO 179/1eU |
23 °C | 39 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 39 kJ/m² | dry | ISO 179/1eU | |
Zugfestigkeit | -40 °C | 220 MPa Show Supplier Material materials with Zugfestigkeit of 220 MPa | dry | ISO 527-1/-2 |
170 MPa Show Supplier Material materials with Zugfestigkeit of 170 MPa | dry | ISO 527-1/-2 | ||
120 °C | 105 MPa Show Supplier Material materials with Zugfestigkeit of 105 MPa | dry | ISO 527-1/-2 | |
160 °C | 75 MPa Show Supplier Material materials with Zugfestigkeit of 75 MPa | dry | ISO 527-1/-2 |
Thermisch
Property | Value | Condition | Testing Standard | Pressure | Comment |
---|---|---|---|---|---|
Glasübergangstemperatur | 90 °C Show Supplier Material materials with Glasübergangstemperatur of 90 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Koeffizient der thermischen Ausdehnung | 1.3e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.3e-07 1/K | dry | ISO 11359-1/-2 | parallel, above Tg | |
1.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.5e-07 1/K | dry | ISO 11359-1/-2 | Parallel | ||
3.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3.5e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
9e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 9e-07 1/K | dry | ISO 11359-1/-2 | normal, above Tg | ||
Schmelzpunkt | 280 °C Show Supplier Material materials with Schmelzpunkt of 280 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 265 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 265 °C | dry | ISO 75-1/-2 | 2 MPa |
Elektrisch
Property | Value | Condition | Testing Standard | Comment |
---|---|---|---|---|
Dielektrizitätskonstante | 4.5 [-] Show Supplier Material materials with Dielektrizitätskonstante of 4.5 [-] | dry | IEC 60250 | 5GHz |
Durchschlagfestigkeit | 26 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 26 kV/mm | dry | IEC 60234 | |
Kriechstromfestigkeit | 175 V Show Supplier Material materials with Kriechstromfestigkeit of 175 V | dry | IEC 60112 | |
Surface resistivity | 1e+15 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq | dry | IEC 62631-3-2 | |
Verlustfaktor | 50 [-] Show Supplier Material materials with Verlustfaktor of 50 [-] | dry | IEC 60250 | 5GHz |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Crankshaft Covers, Rectifier, Water pump part |