Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Dichte | 1.29 g/cm³ Show Supplier Material materials with Dichte of 1.29 g/cm³ | dry | ISO 1183 | |
Wasserabsorption | 0.06 % Show Supplier Material materials with Wasserabsorption of 0.06 % | dry | ISO 62 | at 23°C after 24h |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard |
|---|---|---|---|---|
Biegemodul | 2.7 GPa Show Supplier Material materials with Biegemodul of 2.7 GPa | dry | ISO 178 | |
120 °C | 0.36 GPa Show Supplier Material materials with Biegemodul of 0.36 GPa | dry | ISO 178 | |
160 °C | 0.24 GPa Show Supplier Material materials with Biegemodul of 0.24 GPa | dry | ISO 178 | |
200 °C | 0.2 GPa Show Supplier Material materials with Biegemodul of 0.2 GPa | dry | ISO 178 | |
Dehnung | -40 °C | 2 % Show Supplier Material materials with Dehnung of 2 % | dry | ISO 527-1/-2 |
9 % Show Supplier Material materials with Dehnung of 9 % | dry | ISO 527-1/-2 | ||
Elastizitätsmodul | -40 °C | 3.3 GPa Show Supplier Material materials with Elastizitätsmodul of 3.3 GPa | dry | ISO 527-1/-2 |
2.9 GPa Show Supplier Material materials with Elastizitätsmodul of 2.9 GPa | dry | ISO 527-1/-2 | ||
Elongation at yield | 5 % Show Supplier Material materials with Elongation at yield of 5 % | dry | ISO 527-1/-2 | |
Flexural yield strength | 90 MPa Show Supplier Material materials with Flexural yield strength of 90 MPa | dry | ISO 178 | |
120 °C | 12 MPa Show Supplier Material materials with Flexural yield strength of 12 MPa | dry | ISO 178 | |
160 °C | 8.5 MPa Show Supplier Material materials with Flexural yield strength of 8.5 MPa | dry | ISO 178 | |
200 °C | 7 MPa Show Supplier Material materials with Flexural yield strength of 7 MPa | dry | ISO 178 | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 3.5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 3.5 kJ/m² | dry | ISO 179/1eA |
23 °C | 11 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 11 kJ/m² | dry | ISO 179/1eA | |
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 20 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 20 kJ/m² | dry | ISO 179/1eU |
Zugfestigkeit | -40 °C | 55.0 MPa Show Supplier Material materials with Zugfestigkeit of 55.0 MPa | dry | ISO 527-1/-2 |
60 MPa Show Supplier Material materials with Zugfestigkeit of 60 MPa | dry | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Testing Standard | Pressure | Comment |
|---|---|---|---|---|---|
Entflammbarkeit | V-2 | dry | IEC 60695-11-10 | ||
Glasübergangstemperatur | 90 °C Show Supplier Material materials with Glasübergangstemperatur of 90 °C | dry | ISO 11357-1/-2 | 10°C/min | |
Koeffizient der thermischen Ausdehnung | 6e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6e-07 1/K | dry | ISO 11359-1/-2 | Parallel | |
6.5e-07 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 6.5e-07 1/K | dry | ISO 11359-1/-2 | Normal | ||
1.1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.1e-06 1/K | dry | ISO 11359-1/-2 | parallel, above Tg | ||
1.4e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.4e-06 1/K | dry | ISO 11359-1/-2 | normal, above Tg | ||
Schmelzpunkt | 280 °C Show Supplier Material materials with Schmelzpunkt of 280 °C | dry | ISO 11357-1/-3 | 10°C/min | |
Wärmeformbeständigkeitstemperatur | 102 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 102 °C | dry | ISO 75-1/-2 | 2 MPa |
Elektrisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Dielektrizitätskonstante | 3.2 [-] Show Supplier Material materials with Dielektrizitätskonstante of 3.2 [-] | dry | IEC 60250 | 5GHz |
Durchschlagfestigkeit | 41 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 41 kV/mm | dry | IEC 60243-1 | |
Surface resistivity | 1e+15 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq | dry | IEC 62631-3-2 | |
Verlustfaktor | 23 [-] Show Supplier Material materials with Verlustfaktor of 23 [-] | dry | IEC 60250 | 5GHz |
Volume resistivity | 1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | dry | IEC 62631-3-1 |
Rheological Properties
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Schmelzmassenflussrate | 300 °C | 24.6 g/10min Show Supplier Material materials with Schmelzmassenflussrate of 24.6 g/10min | dry | ISO 1133 | |
Schmelzvolumenflussrate | 300 °C | 21.7 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 21.7 cm³/10min | dry | ISO 1133 | |
Schrumpfung | 1.2 % Show Supplier Material materials with Schrumpfung of 1.2 % | dry | ISO 294-4 | Parallel | |
1.3 % Show Supplier Material materials with Schrumpfung of 1.3 % | dry | ISO 294-4 | Normal |
Technological properties
| Property |
|---|