Eigenschaften
Allgemein
| Property | Value |
|---|---|
Relative Dichte | 8.78 [-] Show Supplier Material materials with Relative Dichte of 8.78 [-] |
Mechanisch
| Property | Value | Comment |
|---|---|---|
Biegemodul | 100 GPa Show Supplier Material materials with Biegemodul of 100 GPa | |
Dehnung | 5 % Show Supplier Material materials with Dehnung of 5 % | min. | SH Temper | for thickness 0.1-0.4 mm |
9 % Show Supplier Material materials with Dehnung of 9 % | min. | EH Temper | for thickness 0.1-0.8 mm | |
11 % Show Supplier Material materials with Dehnung of 11 % | min. | H Temper | for thickness 0.1-1.6 mm | |
Elastizitätsmodul | 105 GPa Show Supplier Material materials with Elastizitätsmodul of 105 GPa | |
Härte, Vickers | 200 - 240 [-] Show Supplier Material materials with Härte, Vickers of 200 - 240 [-] | H Temper | for thickness 0.1-1.6 mm |
230 - 270 [-] Show Supplier Material materials with Härte, Vickers of 230 - 270 [-] | EH Temper | for thickness 0.1-0.8 mm | |
250 - 300 [-] Show Supplier Material materials with Härte, Vickers of 250 - 300 [-] | SH Temper | for thickness 0.1-0.4 mm | |
270 [-] Show Supplier Material materials with Härte, Vickers of 270 [-] | min. | ESH Temper | for thickness 0.1-0.4 mm | |
290 [-] Show Supplier Material materials with Härte, Vickers of 290 [-] | min. | XSH Temper | for thickness 0.1-0.4 mm | |
Streckgrenze | 430 MPa Show Supplier Material materials with Streckgrenze of 430 MPa | min. | H Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm |
510 MPa Show Supplier Material materials with Streckgrenze of 510 MPa | min. | EH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
510 MPa Show Supplier Material materials with Streckgrenze of 510 MPa | min. | H Temper | for thickness 0.1-1.6 mm, RP02 | |
570 MPa Show Supplier Material materials with Streckgrenze of 570 MPa | min. | SH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
630 MPa Show Supplier Material materials with Streckgrenze of 630 MPa | min. | ESH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
630 MPa Show Supplier Material materials with Streckgrenze of 630 MPa | min. | EH Temper | for thickness 0.1-0.8 mm, RP02 | |
700 MPa Show Supplier Material materials with Streckgrenze of 700 MPa | min. | XSH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
750 MPa Show Supplier Material materials with Streckgrenze of 750 MPa | min. | SH Temper | for thickness 0.1-0.4 mm, RP02 | |
870 MPa Show Supplier Material materials with Streckgrenze of 870 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm, RP02 | |
930 MPa Show Supplier Material materials with Streckgrenze of 930 MPa | min. | XSH Temper | for thickness 0.1-0.4 mm, RP02 | |
Zugfestigkeit | 650 - 750 MPa Show Supplier Material materials with Zugfestigkeit of 650 - 750 MPa | H Temper | for thickness 0.1-1.6 mm |
750 - 850 MPa Show Supplier Material materials with Zugfestigkeit of 750 - 850 MPa | EH Temper | for thickness 0.1-0.8 mm | |
850 - 950 MPa Show Supplier Material materials with Zugfestigkeit of 850 - 950 MPa | SH Temper | for thickness 0.1-0.4 mm | |
950 MPa Show Supplier Material materials with Zugfestigkeit of 950 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm | |
1000 MPa Show Supplier Material materials with Zugfestigkeit of 1000 MPa | min. | XSH Temper | for thickness 0.1-0.4 mm |
Thermisch
| Property | Value |
|---|---|
Koeffizient der thermischen Ausdehnung | 1.84e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.84e-05 1/K |
Schmelzpunkt | 845 - 1000 °C Show Supplier Material materials with Schmelzpunkt of 845 - 1000 °C |
Spezifische Wärmekapazität | 375 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 375 J/(kg·K) |
Wärmeleitfähigkeit | 50 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 50 W/(m·K) |
Elektrisch
| Property | Value |
|---|---|
Specific Electrical conductivity | 10 % IACS Show Supplier Material materials with Specific Electrical conductivity of 10 % IACS |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Andere | 99.5 % Show Supplier Material materials with Andere of 99.5 % | min. | Cu+Sn+P |
Blei | 0.02 % Show Supplier Material materials with Blei of 0.02 % | max. |
Eisen | 0.1 % Show Supplier Material materials with Eisen of 0.1 % | max. |
Phosphor | 0.03 - 0.35 % Show Supplier Material materials with Phosphor of 0.03 - 0.35 % | |
Zink | 0.2 % Show Supplier Material materials with Zink of 0.2 % | max. |
Zinn | 9 - 11 % Show Supplier Material materials with Zinn of 9 - 11 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
| Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
| Other | Hardness Vickers note: Minimum test force is 1.961 N | |
| Tolerances | ||