Allgemein
Property | Value |
---|---|
Relative Dichte | 8.8 [-] Show Supplier Material materials with Relative Dichte of 8.8 [-] |
Mechanisch
Property | Value | Comment |
---|---|---|
Biegemodul | 100 GPa Show Supplier Material materials with Biegemodul of 100 GPa | |
Dehnung | 5 % Show Supplier Material materials with Dehnung of 5 % | min. | ESH Temper | for thickness 0.1-0.4 mm |
9 % Show Supplier Material materials with Dehnung of 9 % | min. | SH Temper | for thickness 0.1-1.2 mm | |
11 % Show Supplier Material materials with Dehnung of 11 % | min. | EH Temper | for thickness 0.1-1.2 mm | |
20 % Show Supplier Material materials with Dehnung of 20 % | min. | H Temper | for thickness 0.1-1.6 mm | |
27 % Show Supplier Material materials with Dehnung of 27 % | min. | 1/2H Temper | for thickness 0.1-1.6 mm | |
Elastizitätsmodul | 110 GPa Show Supplier Material materials with Elastizitätsmodul of 110 GPa | |
Härte, Vickers | 140 - 205 [-] Show Supplier Material materials with Härte, Vickers of 140 - 205 [-] | 1/2H Temper | for thickness 0.1-1.6 mm |
185 - 235 [-] Show Supplier Material materials with Härte, Vickers of 185 - 235 [-] | H Temper | for thickness 0.1-1.6 mm | |
210 - 260 [-] Show Supplier Material materials with Härte, Vickers of 210 - 260 [-] | EH Temper | for thickness 0.1-1.2 mm | |
230 - 270 [-] Show Supplier Material materials with Härte, Vickers of 230 - 270 [-] | SH Temper | for thickness 0.1-1.2 mm | |
245 - 285 [-] Show Supplier Material materials with Härte, Vickers of 245 - 285 [-] | ESH Temper | for thickness 0.1-0.4 mm | |
Streckgrenze | 245 MPa Show Supplier Material materials with Streckgrenze of 245 MPa | min. | 1/2H Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm |
260 MPa Show Supplier Material materials with Streckgrenze of 260 MPa | min. | 1/2H Temper | for thickness 0.1-1.6 mm, RP02 | |
390 MPa Show Supplier Material materials with Streckgrenze of 390 MPa | min. | H Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
450 MPa Show Supplier Material materials with Streckgrenze of 450 MPa | min. | H Temper | for thickness 0.1-1.6 mm, RP02 | |
460 MPa Show Supplier Material materials with Streckgrenze of 460 MPa | min. | EH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
510 MPa Show Supplier Material materials with Streckgrenze of 510 MPa | min. | SH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
560 MPa Show Supplier Material materials with Streckgrenze of 560 MPa | min. | ESH Temper | for spring material (Kb0.1) | for thickness 0.15-1.6 mm | |
580 MPa Show Supplier Material materials with Streckgrenze of 580 MPa | min. | EH Temper | for thickness 0.1-1.2 mm, RP02 | |
640 MPa Show Supplier Material materials with Streckgrenze of 640 MPa | min. | SH Temper | for thickness 0.1-1.2 mm, RP02 | |
690 MPa Show Supplier Material materials with Streckgrenze of 690 MPa | min. | ESH Temper | for thickness 0.1-0.4 mm, RP02 | |
Zugfestigkeit | 470 - 610 MPa Show Supplier Material materials with Zugfestigkeit of 470 - 610 MPa | 1/2H Temper | for thickness 0.1-1.6 mm |
590 - 705 MPa Show Supplier Material materials with Zugfestigkeit of 590 - 705 MPa | H Temper | for thickness 0.1-1.6 mm | |
685 - 785 MPa Show Supplier Material materials with Zugfestigkeit of 685 - 785 MPa | EH Temper | for thickness 0.1-1.2 mm | |
735 - 835 MPa Show Supplier Material materials with Zugfestigkeit of 735 - 835 MPa | SH Temper | for thickness 0.1-1.2 mm | |
770 - 885 MPa Show Supplier Material materials with Zugfestigkeit of 770 - 885 MPa | ESH Temper | for thickness 0.1-0.4 mm |
Thermisch
Property | Value |
---|---|
Koeffizient der thermischen Ausdehnung | 1.82e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 1.82e-05 1/K |
Schmelzpunkt | 880 - 1020 °C Show Supplier Material materials with Schmelzpunkt of 880 - 1020 °C |
Spezifische Wärmekapazität | 377 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 377 J/(kg·K) |
Wärmeleitfähigkeit | 63 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 63 W/(m·K) |
Elektrisch
Property | Value |
---|---|
Specific Electrical conductivity | 12 % IACS Show Supplier Material materials with Specific Electrical conductivity of 12 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Andere | 99.5 % Show Supplier Material materials with Andere of 99.5 % | min. | Cu+Sn+P |
Blei | 0.02 % Show Supplier Material materials with Blei of 0.02 % | max. |
Eisen | 0.1 % Show Supplier Material materials with Eisen of 0.1 % | max. |
Phosphor | 0.03 - 0.35 % Show Supplier Material materials with Phosphor of 0.03 - 0.35 % | |
Zink | 0.2 % Show Supplier Material materials with Zink of 0.2 % | max. |
Zinn | 7 - 9 % Show Supplier Material materials with Zinn of 7 - 9 % |
Technological properties
Property | ||
---|---|---|
Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
Other | Hardness Vickers note: Minimum test force is 1.961 N | |
Tolerances |