Propiedades
General
| Property | Value |
|---|---|
Densidad | 7.7 g/cm³ Show Supplier Material materials with Densidad of 7.7 g/cm³ |
Medidas
| Property | Value | Comment |
|---|---|---|
Diámetro | 160 mm Show Supplier Material materials with Diámetro of 160 mm | max. |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Charpy impact energy, V-notch | 25 J Show Supplier Material materials with Charpy impact energy, V-notch of 25 J | ||
Dureza Brinell | 230 [-] Show Supplier Material materials with Dureza Brinell of 230 [-] | annealed | |
Elongación | 13 % Show Supplier Material materials with Elongación of 13 % | A5 | |
Límite elástico | 20 °C | 500 MPa Show Supplier Material materials with Límite elástico of 500 MPa | RP02 |
100 °C | 460 MPa Show Supplier Material materials with Límite elástico of 460 MPa | RP02 | |
150 °C | 445 MPa Show Supplier Material materials with Límite elástico of 445 MPa | RP02 | |
200 °C | 430 MPa Show Supplier Material materials with Límite elástico of 430 MPa | RP02 | |
250 °C | 415 MPa Show Supplier Material materials with Límite elástico of 415 MPa | RP02 | |
300 °C | 395 MPa Show Supplier Material materials with Límite elástico of 395 MPa | RP02 | |
350 °C | 365 MPa Show Supplier Material materials with Límite elástico of 365 MPa | RP02 | |
400 °C | 330 MPa Show Supplier Material materials with Límite elástico of 330 MPa | RP02 | |
Módulo elástico | 20 °C | 215 GPa Show Supplier Material materials with Módulo elástico of 215 GPa | |
100 °C | 212 GPa Show Supplier Material materials with Módulo elástico of 212 GPa | ||
200 °C | 205 GPa Show Supplier Material materials with Módulo elástico of 205 GPa | ||
300 °C | 200 GPa Show Supplier Material materials with Módulo elástico of 200 GPa | ||
400 °C | 190 GPa Show Supplier Material materials with Módulo elástico of 190 GPa | ||
Resistencia a la tracción | 700 - 850 MPa Show Supplier Material materials with Resistencia a la tracción of 700 - 850 MPa |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 460 J/(kg·K) Show Supplier Material materials with Calor específico of 460 J/(kg·K) | ||
Coeficiente de dilatación térmica | 100 °C | 1.05e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.05e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.1e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.1e-05 1/K | for 20°C to the mentioned temperature | |
300 °C | 1.15e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.15e-05 1/K | for 20°C to the mentioned temperature | |
400 °C | 1.2e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.2e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 30 W/(m·K) Show Supplier Material materials with Conductividad térmica of 30 W/(m·K) |
Eléctrico
| Property | Value |
|---|---|
Resistividad eléctrica | 6e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 6e-07 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Azufre | 0.01 - 0.03 % Show Supplier Material materials with Azufre of 0.01 - 0.03 % |
Carbono | 0.16 - 0.25 % Show Supplier Material materials with Carbono of 0.16 - 0.25 % |
Cromo | 12 - 14 % Show Supplier Material materials with Cromo of 12 - 14 % |
Fósforo | 0.04 % Show Supplier Material materials with Fósforo of 0.04 % |
Hierro | Balance |
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % |
Molibdeno | 0.5 % Show Supplier Material materials with Molibdeno of 0.5 % |
Níquel | 0.5 % Show Supplier Material materials with Níquel of 0.5 % |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Automotive industry, Decorative Applications, Hydraulic Equipment, Petrochemical industry, Food and Beverage industry, Mechanical engineering, Cutlery, Blades | |
| Corrosion properties | Average - Good corrosion resistance in moderately corrosive environments that are free of chlorides, such as soaps, detergents and organic acids. Good resistance in oxidising atmospheres up to temperatures of about 600 °C. 1.4021 is not resistant to intergranular corrosion in the asdelivered or as-welded conditions. PRE = 12.0 – 14.0 | |
| General machinability | Good - The machinability of this grade of stainless steel is directly related to its hardness. 1.4021 machines similar to carbon steels of the same hardness. Although it must be realised that the machining parameters will vary depending on the structure/hardness of the steel. | |
| Heat Treatment | Soft annealing: 745-825°C (Cooling in furnace, air) - Hardening: 950-1050°C and quenching in air, polymer, oil - Tempering: 650-750°C | |
| Hot forming | It is formable at 800-1100°C | |
| Processing history | Quenched and tempered, QT 700 | |
| Welding | Good - Preheating of the work piece to a temperature within the range 100 °C – 300 °C is required as well as a post weld tempering treatment when welding is performed using a matching filler material. Generally, Novonit® 4551 is recommended when a filler material is required. Tempering at 650 °C after welding is recommended to restore some of the ductility in the weld zone. When using an inert or protective shielding gas during welding, care must be taken to avoid use of any hydrogen or nitrogen containing gases since contamination of the weld with nitrogen or hydrogen will adversely affect the mechanical properties. After welding the work piece must be cooled to below the martensite start (MS), temperature of approximately 120 °C before being tempered. | |