General
Property | Value |
---|---|
Densidad | 7.8 g/cm³ Show Supplier Material materials with Densidad of 7.8 g/cm³ |
Medidas
Property | Value | Comment |
---|---|---|
Diámetro | 100 mm Show Supplier Material materials with Diámetro of 100 mm | max. |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy, V-notch | 75 J Show Supplier Material materials with Charpy impact energy, V-notch of 75 J | ||
Dureza Brinell | 360 [-] Show Supplier Material materials with Dureza Brinell of 360 [-] | annealed | |
Elongación | 18 % Show Supplier Material materials with Elongación of 18 % | A5 | |
Límite elástico | 20 °C | 520 MPa Show Supplier Material materials with Límite elástico of 520 MPa | RP02 |
100 °C | 500 MPa Show Supplier Material materials with Límite elástico of 500 MPa | RP02 | |
150 °C | 490 MPa Show Supplier Material materials with Límite elástico of 490 MPa | RP02 | |
200 °C | 480 MPa Show Supplier Material materials with Límite elástico of 480 MPa | RP02 | |
250 °C | 470 MPa Show Supplier Material materials with Límite elástico of 470 MPa | RP02 | |
300 °C | 460 MPa Show Supplier Material materials with Límite elástico of 460 MPa | RP02 | |
Módulo elástico | 20 °C | 200 GPa Show Supplier Material materials with Módulo elástico of 200 GPa | |
100 °C | 195 GPa Show Supplier Material materials with Módulo elástico of 195 GPa | ||
200 °C | 185 GPa Show Supplier Material materials with Módulo elástico of 185 GPa | ||
300 °C | 175 GPa Show Supplier Material materials with Módulo elástico of 175 GPa | ||
400 °C | 170 GPa Show Supplier Material materials with Módulo elástico of 170 GPa | ||
Resistencia a la tracción | 800 - 950 MPa Show Supplier Material materials with Resistencia a la tracción of 800 - 950 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 500 J/(kg·K) Show Supplier Material materials with Calor específico of 500 J/(kg·K) | ||
Coeficiente de dilatación térmica | 100 °C | 1.09e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.09e-05 1/K | for 20°C to the mentioned temperature |
200 °C | 1.11e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.11e-05 1/K | for 20°C to the mentioned temperature | |
Conductividad térmica | 16 W/(m·K) Show Supplier Material materials with Conductividad térmica of 16 W/(m·K) |
Eléctrico
Property | Value |
---|---|
Resistividad eléctrica | 7.1e-07 Ω·m Show Supplier Material materials with Resistividad eléctrica of 7.1e-07 Ω·m |
Chemical properties
Property | Value |
---|---|
Azufre | 0.03 % Show Supplier Material materials with Azufre of 0.03 % |
Carbono | 0.07 % Show Supplier Material materials with Carbono of 0.07 % |
Cobre | 3 - 5 % Show Supplier Material materials with Cobre of 3 - 5 % |
Cromo | 15 - 17 % Show Supplier Material materials with Cromo of 15 - 17 % |
Fósforo | 0.04 % Show Supplier Material materials with Fósforo of 0.04 % |
Hierro | Balance |
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % |
Molibdeno | 0.6 % Show Supplier Material materials with Molibdeno of 0.6 % |
Níquel | 3 - 5 % Show Supplier Material materials with Níquel of 3 - 5 % |
Otro | 0.15 - 0.45 % Show Supplier Material materials with Otro of 0.15 - 0.45 % |
Silicona | 0.7 % Show Supplier Material materials with Silicona of 0.7 % |
Technological properties
Property | ||
---|---|---|
Application areas | Aerospace, Plant engineering and construction, Chemical industry, Wood industry, Mechanical engineering, Oil industry, Paper industry, Sports and leisure industry, Ship building | |
Corrosion properties | The good combination of high corrosion resistance and good mechanical properties makes Acidur 4542 suitable for use in marine environments. In standing seawater, however, Acidur 4542 is susceptible to crevice corrosion. If application in standing seawater cannot be excluded, additional protection (e.g. painting) must be applied. | |
General machinability | Acidur 4542 can be machined in both the solution annealed and hardened condition. The machinability of Acidur 4542 depends on the hardness | |
Heat Treatment | Hardening:1030-1055°C in oil, air - Percipitation hardening: 2 hr 760°C in air / 4 hr 620°C in air | |
Hot forming | It is formable at 900-1150°C | |
Processing history | Percipitation hardened P800 | |
Welding | To weld Acidur 4542, the condition of the base material must be taken into account. The copper is present in the material in a stable form and therefore does not promote hot cracking. In addition to setting optimum welding conditions, care must be taken to avoid undercuts or other welding defects that lead to the formation of a notch. After welding, the material must be solution annealed again within a very short time with subsequent ageing to prevent stress cracking. |