General
Property | Value |
---|---|
Densidad relativa | 8.86 [-] Show Supplier Material materials with Densidad relativa of 8.86 [-] |
Mecánica
Property | Value | Comment |
---|---|---|
Dureza Vickers | 80 - 150 [-] Show Supplier Material materials with Dureza Vickers of 80 - 150 [-] | 1/4H Temper | for thickness 0.15-5 mm |
120 - 180 [-] Show Supplier Material materials with Dureza Vickers of 120 - 180 [-] | 1/2H Temper | for thickness 0.1-5 mm | |
150 - 200 [-] Show Supplier Material materials with Dureza Vickers of 150 - 200 [-] | H Temper | for thickness 0.1-5 mm | |
170 - 220 [-] Show Supplier Material materials with Dureza Vickers of 170 - 220 [-] | EH Temper | for thickness 0.05-5 mm | |
200 [-] Show Supplier Material materials with Dureza Vickers of 200 [-] | min. | SH Temper | for thickness 0.05-5 mm | |
Elongación | 3 % Show Supplier Material materials with Elongación of 3 % | min. | EH Temper | for thickness 0.2-5 mm |
7 % Show Supplier Material materials with Elongación of 7 % | min. | H Temper | for thickness 0.1-5 mm | |
12 % Show Supplier Material materials with Elongación of 12 % | min. | 1/2H Temper | for thickness 0.1-5 mm | |
25 % Show Supplier Material materials with Elongación of 25 % | min. | 1/4H Temper | for thickness 0.1-5 mm | |
38 % Show Supplier Material materials with Elongación of 38 % | min. | O Temper | for thickness 0.1-5 mm | |
Módulo de flexión | 110 GPa Show Supplier Material materials with Módulo de flexión of 110 GPa | |
Módulo elástico | 115 GPa Show Supplier Material materials with Módulo elástico of 115 GPa | |
Resistencia a la tracción | 295 MPa Show Supplier Material materials with Resistencia a la tracción of 295 MPa | min. | O Temper | for thickness 0.1-5 mm |
345 - 440 MPa Show Supplier Material materials with Resistencia a la tracción of 345 - 440 MPa | 1/4H Temper | for thickness 0.1-5 mm | |
410 - 510 MPa Show Supplier Material materials with Resistencia a la tracción of 410 - 510 MPa | 1/2H Temper | for thickness 0.1-5 mm | |
490 - 590 MPa Show Supplier Material materials with Resistencia a la tracción of 490 - 590 MPa | H Temper | for thickness 0.1-5 mm | |
570 - 660 MPa Show Supplier Material materials with Resistencia a la tracción of 570 - 660 MPa | EH Temper | for thickness 0.1-5 mm | |
640 MPa Show Supplier Material materials with Resistencia a la tracción of 640 MPa | min. | SH Temper | for thickness 0.1-5 mm |
Aplicaciones térmicas
Property | Value |
---|---|
Calor específico | 377 J/(kg·K) Show Supplier Material materials with Calor específico of 377 J/(kg·K) |
Coeficiente de dilatación térmica | 1.78e-05 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.78e-05 1/K |
Conductividad térmica | 84 W/(m·K) Show Supplier Material materials with Conductividad térmica of 84 W/(m·K) |
Temperatura de fusión | 975 - 1060 °C Show Supplier Material materials with Temperatura de fusión of 975 - 1060 °C |
Eléctrico
Property | Value |
---|---|
Specific Electrical conductivity | 20 % IACS Show Supplier Material materials with Specific Electrical conductivity of 20 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Estaño | 3.5 - 4.5 % Show Supplier Material materials with Estaño of 3.5 - 4.5 % | |
Fósforo | 0.03 - 0.35 % Show Supplier Material materials with Fósforo of 0.03 - 0.35 % | |
Hierro | 0.1 % Show Supplier Material materials with Hierro of 0.1 % | max. |
Otro | 99.5 % Show Supplier Material materials with Otro of 99.5 % | min. | Cu+Sn+P |
Plomo | 0.02 % Show Supplier Material materials with Plomo of 0.02 % | max. |
Zinc | 0.2 % Show Supplier Material materials with Zinc of 0.2 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | The grade is particularly suitable for electronics (connectors, lead frames, lead terminals, transistor terminals, etc.), electrical (relay and switch contacts, rotary switch slides and contacts, fuse clips, etc.), automotive (bearing frames, hydraulic equipment caps, packing, bearings, clutch disks, electrical parts, etc.) and others (bellows, slides, blades, plate springs, corrosion-proof machinery equipment, diaphragms, etc.) | |
Coating | Standard product specification of a HOT-DIP-tinned strip. *Width means the slit width after plating. *Different plating thickness for each side is possible. * We can accommodate our products to individual specifications other than the above standard specifications. Please feel free to call us. | |
Other | Hardness Vickers note: Minimum test force is 1.961 N | |
Tolerances |