General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.1 g/cm³ Show Supplier Material materials with Densidad of 8.1 g/cm³ |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Azufre | 5E-3 % Show Supplier Material materials with Azufre of 5E-3 % | max. | |
Carbono | 0.02 % Show Supplier Material materials with Carbono of 0.02 % | max. | |
Cobre | 0.8 - 1 % Show Supplier Material materials with Cobre of 0.8 - 1 % | ||
Cromo | 20 - 21 % Show Supplier Material materials with Cromo of 20 - 21 % | ||
Fósforo | 0.03 % Show Supplier Material materials with Fósforo of 0.03 % | max. | |
Hierro | Balance | ||
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % | max. | |
Molibdeno | 6 - 6.8 % Show Supplier Material materials with Molibdeno of 6 - 6.8 % | ||
Nitrógeno | 0.18 - 0.2 % Show Supplier Material materials with Nitrógeno of 0.18 - 0.2 % | ||
Níquel | 24.5 - 25.5 % Show Supplier Material materials with Níquel of 24.5 - 25.5 % | ||
Silicona | 0.5 % Show Supplier Material materials with Silicona of 0.5 % | max. |
Technological properties
Property | ||
---|---|---|
Application areas | 1.4529 is mainly in following applications: Approval for pressure vessels with temperatures between -196 and 400 ° C Building construction approval for components and fasteners made of stainless steel, German Institute of Structural Engineering, September '98 | |
Corrosion properties | 6Mo has excellent general corrosion resistance and improved resistance to pitting and crevice corrosion. The resistance to stress corrosion cracking is also increased. It is often referred as super austenitic stainless steel. Generally it has the following corrosion properties: | |
Hot forming | The material is hot formed within a temperature range of 1200 and 900 ° C and afterwards quenched rapidly in water or air. The annealing tALes place at 1200 ° C. After hot forming, heat treatment for optimum corrosion resistance is recommended. | |
Other | The material Alloy 6XN (UNS N08367) was developed in the USA. This has an almost identical composition and is used in the same applications. However, this material is not listed in the VdTÜV sheet and does not have its own Werkstoffnummer. An use in European pressure applications is therefore difficult. The almost identical material is once used in Europe as 1.4529 and in the USA as UNS N08367. At Hempel, we have therefore stocked the material with double certification so that it can be used internationally. |