General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 7.7 g/cm³ Show Supplier Material materials with Densidad of 7.7 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Brinell | 23.0 °C | 200 [-] Show Supplier Material materials with Dureza Brinell of 200 [-] | min. |
Elongación A5 | 23.0 °C | 18 % Show Supplier Material materials with Elongación A5 of 18 % | min. |
Límite elástico Rp 0,2 | 23.0 °C | 200 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 200 MPa | min. |
Módulo elástico | 23.0 °C | 220 GPa Show Supplier Material materials with Módulo elástico of 220 GPa | |
Resistencia a la tracción | 23.0 °C | 420 - 600 MPa Show Supplier Material materials with Resistencia a la tracción of 420 - 600 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 23.0 °C | 460 J/(kg·K) Show Supplier Material materials with Calor específico of 460 J/(kg·K) |
Conductividad térmica | 23.0 °C | 25 W/(m·K) Show Supplier Material materials with Conductividad térmica of 25 W/(m·K) |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 23.0 °C | 6E-7 Ω·m Show Supplier Material materials with Resistividad eléctrica of 6E-7 Ω·m |
Magnético
Property | Value |
---|---|
Magnetic properties | Magnetisation is possible |
Chemical properties
Property | Value | Comment |
---|---|---|
Azufre | 0.015 % Show Supplier Material materials with Azufre of 0.015 % | max. |
Carbono | 0.03 % Show Supplier Material materials with Carbono of 0.03 % | max. |
Cromo | 17.5 - 18.5 % Show Supplier Material materials with Cromo of 17.5 - 18.5 % | |
Fósforo | 0.04 % Show Supplier Material materials with Fósforo of 0.04 % | max. |
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % | max. |
Niobio | 0.3 % Show Supplier Material materials with Niobio of 0.3 % | max. |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % | max. |
Titanio | 0.1 - 0.6 % Show Supplier Material materials with Titanio of 0.1 - 0.6 % |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive Industry, Catalysts and exhaust systems, Mechanical Engineering, Plant construction, Chemical & petrochemical, Apparatus and tank construction | |
Corrosion properties | Excellent stress corrosion cracking resistance | |
Solution annealing | 750-850°C | |
Welding | TIG welding: satisfactory, MAG Solid wire: satisfactory, Arc welding: satisfactory, UP welding: satisfactory, Laser beam welding: satisfactory, Gas fusion welding: limited. A thermal treatment after welding is recommended. | |
Workability | Hot forming: 800-1100°C |