General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 7.7 g/cm³ Show Supplier Material materials with Densidad of 7.7 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Brinell | 23.0 °C | 200 [-] Show Supplier Material materials with Dureza Brinell of 200 [-] | max. |
Elongación A5 | 23.0 °C | 20 % Show Supplier Material materials with Elongación A5 of 20 % | min. |
Límite elástico Rp 0,2 | 23.0 °C | 320 MPa Show Supplier Material materials with Límite elástico Rp 0,2 of 320 MPa | min. |
Módulo elástico | 23.0 °C | 220 GPa Show Supplier Material materials with Módulo elástico of 220 GPa | |
Resistencia a la tracción | 23.0 °C | 450 - 650 MPa Show Supplier Material materials with Resistencia a la tracción of 450 - 650 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 23.0 °C | 430 J/(kg·K) Show Supplier Material materials with Calor específico of 430 J/(kg·K) |
Conductividad térmica | 23.0 °C | 23 W/(m·K) Show Supplier Material materials with Conductividad térmica of 23 W/(m·K) |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 23.0 °C | 8E-7 Ω·m Show Supplier Material materials with Resistividad eléctrica of 8E-7 Ω·m |
Magnético
Property | Value |
---|---|
Magnetic properties | Magnetisation is possible |
Chemical properties
Property | Value | Comment |
---|---|---|
Azufre | 0.015 % Show Supplier Material materials with Azufre of 0.015 % | max. |
Carbono | 0.025 % Show Supplier Material materials with Carbono of 0.025 % | max. |
Cromo | 17 - 20 % Show Supplier Material materials with Cromo of 17 - 20 % | |
Fósforo | 0.04 % Show Supplier Material materials with Fósforo of 0.04 % | max. |
Manganeso | 1 % Show Supplier Material materials with Manganeso of 1 % | max. |
Molibdeno | 1.8 - 2.5 % Show Supplier Material materials with Molibdeno of 1.8 - 2.5 % | |
Nitrógeno | 0.03 % Show Supplier Material materials with Nitrógeno of 0.03 % | max. |
Silicona | 1 % Show Supplier Material materials with Silicona of 1 % | max. |
Titanio | 0.8 % Show Supplier Material materials with Titanio of 0.8 % | max., (min: 4x(C+N)+0.15) |
Technological properties
Property | ||
---|---|---|
Application areas | Automotive Industry, Fasteners, Mechanical Engineering, Plant construction, Armature construction, Apparatus and tank construction, Home appliances | |
Corrosion properties | Very good resistance against pitting corrosion | |
General machinability | Good | |
Polishing ability | Bad | |
Solution annealing | 750-900°C | |
Welding | TIG welding: suitable, MAG Solid wire: suitable, Arc welding: suitable, UP welding: limited, Laser beam welding: suitable, Gas fusion welding: not suitable. A heat inpute should be as low as possible. | |
Workability | Hot forming: 750-1150°C |