General
Property | Temperature | Value | |
---|---|---|---|
Density | 23.0 °C | 1.78 g/cm³ Show Supplier Material materials with Density of 1.78 g/cm³ | |
Particle size range | 0.76 µm Show Supplier Material materials with Particle size range of 0.76 µm | ||
Particle size | max. |
Mechanical
Property | Temperature | Value |
---|---|---|
Compressive strength | 23.0 °C | 55.02 MPa Show Supplier Material materials with Compressive strength of 55.02 MPa |
Compressive strength, transverse | 23.0 °C | 55.02 MPa Show Supplier Material materials with Compressive strength, transverse of 55.02 MPa |
Elastic modulus | 23.0 °C | 10.96 GPa Show Supplier Material materials with Elastic modulus of 10.96 GPa |
Elastic modulus, transverse | 23.0 °C | 8.27 GPa Show Supplier Material materials with Elastic modulus, transverse of 8.27 GPa |
Flexural strength | 23.0 °C | 24.03 MPa Show Supplier Material materials with Flexural strength of 24.03 MPa |
Flexural strength, transverse | 23.0 °C | 20.01 MPa Show Supplier Material materials with Flexural strength, transverse of 20.01 MPa |
Hardness, Rockwell R | 23.0 °C | 93 [-] Show Supplier Material materials with Hardness, Rockwell R of 93 [-] |
Tensile strength | 23.0 °C | 19.02 MPa Show Supplier Material materials with Tensile strength of 19.02 MPa |
Tensile strength, transverse | 23.0 °C | 15 MPa Show Supplier Material materials with Tensile strength, transverse of 15 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ash content | 23.0 °C | 0.12 % Show Supplier Material materials with Ash content of 0.12 % | |
Coefficient of thermal expansion | 23.0 °C | 2.5E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-6 1/K | average for 20-100°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 3.6E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.6E-6 1/K | average for 20-100°C |
Thermal conductivity, in-plane | 23.0 °C | 170 W/(m·K) Show Supplier Material materials with Thermal conductivity, in-plane of 170 W/(m·K) | |
Thermal conductivity, through-plane | 23.0 °C | 130 W/(m·K) Show Supplier Material materials with Thermal conductivity, through-plane of 130 W/(m·K) |
Electrical
Technological properties
Property | ||
---|---|---|
Application areas | Casting molds and furnace parts for hot metal, Powder metallurgy, Boats and trays for sintering applications, Resistance heating, Crucibles for melting and alloying, Quartz processing | |
Processing history | Extruded |