Graphite CS114

Alternative and trade names
CS114
Want to keep this datasheet? Save it now in your required format

Description

CS-114 graphite has a specially engineered treatment to reduce oxidation at temperatures up to 750°C. This anti-oxidation graphite has been shown to increase lifetime 6 to 10 times greater than standard graphite materials in oxygen rich applications operating up to 750°C. CS-114 graphite is good for all applications requiring high densities, good mechanical properties, as well as oxidation protection.

This material data has been provided by Advanced Graphite Materials.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

23.0 °C

1.74 g/cm³

Show Supplier Material materials with Density of 1.74 g/cm³

Particle size range

0.76 µm

Show Supplier Material materials with Particle size range of 0.76 µm

Particle size

max.

Mechanical

PropertyTemperatureValue

Compressive strength

23.0 °C

46.1 MPa

Show Supplier Material materials with Compressive strength of 46.1 MPa

Compressive strength, transverse

23.0 °C

46.1 MPa

Show Supplier Material materials with Compressive strength, transverse of 46.1 MPa

Elastic modulus

23.0 °C

10.98 GPa

Show Supplier Material materials with Elastic modulus of 10.98 GPa

Elastic modulus, transverse

23.0 °C

8.23 GPa

Show Supplier Material materials with Elastic modulus, transverse of 8.23 GPa

Flexural strength

23.0 °C

21.08 MPa

Show Supplier Material materials with Flexural strength of 21.08 MPa

Flexural strength, transverse

23.0 °C

15.7 MPa

Show Supplier Material materials with Flexural strength, transverse of 15.7 MPa

Hardness, Rockwell R

23.0 °C

83 [-]

Show Supplier Material materials with Hardness, Rockwell R of 83 [-]

Tensile strength

23.0 °C

14.71 MPa

Show Supplier Material materials with Tensile strength of 14.71 MPa

Tensile strength, transverse

23.0 °C

10.79 MPa

Show Supplier Material materials with Tensile strength, transverse of 10.79 MPa

Thermal

PropertyTemperatureValueComment

Ash content

23.0 °C

0.09 %

Show Supplier Material materials with Ash content of 0.09 %

Coefficient of thermal expansion

23.0 °C

2.5E-6 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-6 1/K

average for 20-100°C

Coefficient of thermal expansion, transverse

23.0 °C

3.6E-6 1/K

Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.6E-6 1/K

average for 20-100°C

Thermal conductivity, in-plane

23.0 °C

160 W/(m·K)

Show Supplier Material materials with Thermal conductivity, in-plane of 160 W/(m·K)

Thermal conductivity, through-plane

23.0 °C

145 W/(m·K)

Show Supplier Material materials with Thermal conductivity, through-plane of 145 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical resistivity

23.0 °C

7.1E-6 Ω·m

Show Supplier Material materials with Electrical resistivity of 7.1E-6 Ω·m

Electrical resistivity, transverse

23.0 °C

9.4E-6 Ω·m

Show Supplier Material materials with Electrical resistivity, transverse of 9.4E-6 Ω·m

Technological properties

Property
Application areas

Aluminum pumps, Aluminum dispersers/impellers, Aluminum degassing shapes/rotors, Aluminum degassing volute case/rotors, Casting molds and furnace parts

Processing history

Extruded