Properties
General
| Property | Temperature | Value | |
|---|---|---|---|
Density | 23.0 °C | 1.63 g/cm³ Show Supplier Material materials with Density of 1.63 g/cm³ | |
Particle size range | 0.76 µm Show Supplier Material materials with Particle size range of 0.76 µm | ||
Particle size | max. | ||
Mechanical
| Property | Temperature | Value |
|---|---|---|
Compressive strength, transverse | 23.0 °C | 34 MPa Show Supplier Material materials with Compressive strength, transverse of 34 MPa |
Elastic modulus, transverse | 23.0 °C | 6.9 GPa Show Supplier Material materials with Elastic modulus, transverse of 6.9 GPa |
Flexural strength, transverse | 23.0 °C | 13.44 MPa Show Supplier Material materials with Flexural strength, transverse of 13.44 MPa |
Hardness, Rockwell R | 23.0 °C | 32 [-] Show Supplier Material materials with Hardness, Rockwell R of 32 [-] |
Tensile strength, transverse | 23.0 °C | 9 MPa Show Supplier Material materials with Tensile strength, transverse of 9 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Ash content | 23.0 °C | 0.12 % Show Supplier Material materials with Ash content of 0.12 % | |
Coefficient of thermal expansion | 23.0 °C | 3.6E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.6E-6 1/K | average for 20-100°C |
Thermal conductivity, through-plane | 23.0 °C | 130 W/(m·K) Show Supplier Material materials with Thermal conductivity, through-plane of 130 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity, transverse | 23.0 °C | 9.3E-6 Ω·m Show Supplier Material materials with Electrical resistivity, transverse of 9.3E-6 Ω·m |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Pressure casting molds, Centrifugal casting molds, Large diameter susceptors | |
| Processing history | Pressure molded | |