General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 1.83 g/cm³ Show Supplier Material materials with Density of 1.83 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Compressive strength | 23.0 °C | 100 MPa Show Supplier Material materials with Compressive strength of 100 MPa |
Elastic modulus | 23.0 °C | 11.5 GPa Show Supplier Material materials with Elastic modulus of 11.5 GPa |
Flexural strength | 23.0 °C | 60 MPa Show Supplier Material materials with Flexural strength of 60 MPa |
Hardness, Rockwell H | 23.0 °C | 70 [-] Show Supplier Material materials with Hardness, Rockwell H of 70 [-] |
Hardness, Rockwell L | 23.0 °C | 100 [-] Show Supplier Material materials with Hardness, Rockwell L of 100 [-] |
Tensile strength | 23.0 °C | 40 MPa Show Supplier Material materials with Tensile strength of 40 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ash content | 23.0 °C | 0.02 % Show Supplier Material materials with Ash content of 0.02 % | |
Coefficient of thermal expansion | 23.0 °C | 3.2E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.2E-6 1/K | average for 20-100°C |
Thermal conductivity, in-plane | 23.0 °C | 95 W/(m·K) Show Supplier Material materials with Thermal conductivity, in-plane of 95 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 1.3E-5 Ω·m Show Supplier Material materials with Electrical resistivity of 1.3E-5 Ω·m |
Technological properties
Property | ||
---|---|---|
Application areas | Continuous casting dies, Hot pressing dies and molds | |
Processing history | Isomolded |