Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 1.82 g/cm³ Show Supplier Material materials with Density of 1.82 g/cm³ |
Mechanical
Property | Temperature | Value |
---|---|---|
Compressive strength | 23.0 °C | 85 MPa Show Supplier Material materials with Compressive strength of 85 MPa |
Elastic modulus | 23.0 °C | 12 GPa Show Supplier Material materials with Elastic modulus of 12 GPa |
Flexural strength | 23.0 °C | 50 MPa Show Supplier Material materials with Flexural strength of 50 MPa |
Hardness, Rockwell L | 23.0 °C | 90 [-] Show Supplier Material materials with Hardness, Rockwell L of 90 [-] |
Tensile strength | 23.0 °C | 32 MPa Show Supplier Material materials with Tensile strength of 32 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ash content | 23.0 °C | 0.08 % Show Supplier Material materials with Ash content of 0.08 % | |
Coefficient of thermal expansion | 23.0 °C | 3.2E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.2E-6 1/K | average for 20-100°C |
Thermal conductivity, in-plane | 23.0 °C | 120 W/(m·K) Show Supplier Material materials with Thermal conductivity, in-plane of 120 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 1.05E-5 Ω·m Show Supplier Material materials with Electrical resistivity of 1.05E-5 Ω·m |
Technological properties
Property | ||
---|---|---|
Application areas | Continuous casting dies, Hot pressing dies and molds | |
Processing history | Isomolded |