General
Property | Temperature | Value | |
---|---|---|---|
Density | 23.0 °C | 1.62 g/cm³ Show Supplier Material materials with Density of 1.62 g/cm³ | |
Particle size range | 0.76 µm Show Supplier Material materials with Particle size range of 0.76 µm | ||
Particle size | max. |
Mechanical
Property | Temperature | Value |
---|---|---|
Compressive strength | 23.0 °C | 26.5 MPa Show Supplier Material materials with Compressive strength of 26.5 MPa |
Compressive strength, transverse | 23.0 °C | 27.6 MPa Show Supplier Material materials with Compressive strength, transverse of 27.6 MPa |
Elastic modulus | 23.0 °C | 8.68 GPa Show Supplier Material materials with Elastic modulus of 8.68 GPa |
Elastic modulus, transverse | 23.0 °C | 6.55 GPa Show Supplier Material materials with Elastic modulus, transverse of 6.55 GPa |
Flexural strength | 23.0 °C | 14.1 MPa Show Supplier Material materials with Flexural strength of 14.1 MPa |
Flexural strength, transverse | 23.0 °C | 12.4 MPa Show Supplier Material materials with Flexural strength, transverse of 12.4 MPa |
Tensile strength | 23.0 °C | 9.27 MPa Show Supplier Material materials with Tensile strength of 9.27 MPa |
Tensile strength, transverse | 23.0 °C | 8.27 MPa Show Supplier Material materials with Tensile strength, transverse of 8.27 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ash content | 23.0 °C | 0.9 % Show Supplier Material materials with Ash content of 0.9 % | |
Coefficient of thermal expansion | 23.0 °C | 2.02E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.02E-6 1/K | average for 20-100°C |
Thermal conductivity, in-plane | 23.0 °C | 140 W/(m·K) Show Supplier Material materials with Thermal conductivity, in-plane of 140 W/(m·K) | |
Thermal conductivity, through-plane | 23.0 °C | 125 W/(m·K) Show Supplier Material materials with Thermal conductivity, through-plane of 125 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 8.51E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 8.51E-6 Ω·m |
Technological properties
Property | ||
---|---|---|
Application areas | Furnace parts | |
Processing history | Extruded |