General
Property | Temperature | Value | |
---|---|---|---|
Density | 23.0 °C | 1.65 g/cm³ Show Supplier Material materials with Density of 1.65 g/cm³ | |
Particle size range | 0.76 µm Show Supplier Material materials with Particle size range of 0.76 µm | ||
Porosity | 18 % Show Supplier Material materials with Porosity of 18 % | ||
Particle size | max. |
Mechanical
Property | Temperature | Value |
---|---|---|
Compressive strength | 23.0 °C | 46 MPa Show Supplier Material materials with Compressive strength of 46 MPa |
Compressive strength, transverse | 23.0 °C | 46 MPa Show Supplier Material materials with Compressive strength, transverse of 46 MPa |
Elastic modulus | 23.0 °C | 9.6 GPa Show Supplier Material materials with Elastic modulus of 9.6 GPa |
Elastic modulus, transverse | 23.0 °C | 7.5 GPa Show Supplier Material materials with Elastic modulus, transverse of 7.5 GPa |
Flexural strength | 23.0 °C | 17 MPa Show Supplier Material materials with Flexural strength of 17 MPa |
Flexural strength, transverse | 23.0 °C | 13 MPa Show Supplier Material materials with Flexural strength, transverse of 13 MPa |
Tensile strength | 23.0 °C | 13 MPa Show Supplier Material materials with Tensile strength of 13 MPa |
Tensile strength, transverse | 23.0 °C | 8.9 MPa Show Supplier Material materials with Tensile strength, transverse of 8.9 MPa |
Thermal
Property | Temperature | Value | Comment |
---|---|---|---|
Ash content | 23.0 °C | 0.12 % Show Supplier Material materials with Ash content of 0.12 % | |
Coefficient of thermal expansion | 23.0 °C | 2.5E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.5E-6 1/K | average for 20-100°C |
Coefficient of thermal expansion, transverse | 23.0 °C | 3.5E-6 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 3.5E-6 1/K | average for 20-100°C |
Thermal conductivity, in-plane | 23.0 °C | 145 W/(m·K) Show Supplier Material materials with Thermal conductivity, in-plane of 145 W/(m·K) | |
Thermal conductivity, through-plane | 23.0 °C | 130 W/(m·K) Show Supplier Material materials with Thermal conductivity, through-plane of 130 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical resistivity | 23.0 °C | 6.8E-6 Ω·m Show Supplier Material materials with Electrical resistivity of 6.8E-6 Ω·m |
Electrical resistivity, transverse | 23.0 °C | 9.4E-6 Ω·m Show Supplier Material materials with Electrical resistivity, transverse of 9.4E-6 Ω·m |
Technological properties
Property | ||
---|---|---|
Application areas | Diamond Drill Bit Mold Material |