Properties
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Density | 23.0 °C | 8.9 g/cm³ Show Material materials with Density of 8.9 g/cm³ | Typical for Wrought Copper Pure / Low Alloyed Copper |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 95 - 98 GPa Show Material materials with Elastic modulus of 95 - 98 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Elongation | 23.0 °C | 30 % Show Material materials with Elongation of 30 % | |
Poisson's ratio | 23.0 °C | 0.34 [-] Show Material materials with Poisson's ratio of 0.34 [-] | Typical for Wrought Copper Pure / Low Alloyed Copper |
Shear modulus | 23.0 °C | 48 GPa Show Material materials with Shear modulus of 48 GPa | Typical for Wrought Copper Pure / Low Alloyed Copper |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.6E-5 - 1.8E-5 1/K Show Material materials with Coefficient of thermal expansion of 1.6E-5 - 1.8E-5 1/K | Typical for Wrought Copper Pure / Low Alloyed Copper |
Melting point | 1083 °C Show Material materials with Melting point of 1083 °C | ||
Specific heat capacity | 23.0 °C | 377 - 420 J/(kg·K) Show Material materials with Specific heat capacity of 377 - 420 J/(kg·K) | Typical for Wrought Copper Pure / Low Alloyed Copper |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 5.86E+7 S/m Show Material materials with Electrical conductivity of 5.86E+7 S/m |
Electrical resistivity | 23.0 °C | 1.71E-8 Ω·m Show Material materials with Electrical resistivity of 1.71E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Antimony | 4E-4 % Show Material materials with Antimony of 4E-4 % |
Arsenic | 5E-4 % Show Material materials with Arsenic of 5E-4 % |
Bismuth | 2E-4 % Show Material materials with Bismuth of 2E-4 % |
Cadmium | 1E-4 % Show Material materials with Cadmium of 1E-4 % |
Copper | 99.99 % Show Material materials with Copper of 99.99 % |
Iron | 1E-3 % Show Material materials with Iron of 1E-3 % |
Lead | 5E-4 % Show Material materials with Lead of 5E-4 % |
Manganese | 5E-4 % Show Material materials with Manganese of 5E-4 % |
Nickel | 1E-3 % Show Material materials with Nickel of 1E-3 % |
Phosphorus | 3E-3 % Show Material materials with Phosphorus of 3E-3 % |
Silver | 2.5E-3 % Show Material materials with Silver of 2.5E-3 % |
Sulfur | 1.5E-3 % Show Material materials with Sulfur of 1.5E-3 % |
Tellurium | 2E-4 % Show Material materials with Tellurium of 2E-4 % |
Tin | 2E-4 % Show Material materials with Tin of 2E-4 % |
Zinc | 1E-4 % Show Material materials with Zinc of 1E-4 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | hard brazing : very good, soft brazing: very good | |
| Workability | Cold forming degree between anneals: max. 95 %, general (condition): very good | |