Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 8.1 g/cm³ Show Material materials with Density of 8.1 g/cm³ |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 93 GPa Show Material materials with Elastic modulus of 93 GPa |
Elongation | 23.0 °C | 15 % Show Material materials with Elongation of 15 % |
Hardness, Brinell | 23.0 °C | 150 [-] Show Material materials with Hardness, Brinell of 150 [-] |
Hardness, Vickers | 23.0 °C | 150 [-] Show Material materials with Hardness, Vickers of 150 [-] |
Tensile strength | 23.0 °C | 540 MPa Show Material materials with Tensile strength of 540 MPa |
Yield strength Rp0.2 | 23.0 °C | 280 MPa Show Material materials with Yield strength Rp0.2 of 280 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 20.0 °C | 2.04E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.04E-5 1/K |
100.0 °C | 2.04E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.04E-5 1/K | |
Melting point | 865 - 885 °C Show Material materials with Melting point of 865 - 885 °C | |
Thermal conductivity | 23.0 °C | 63 W/(m·K) Show Material materials with Thermal conductivity of 63 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 7.80E+6 S/m Show Material materials with Electrical conductivity of 7.80E+6 S/m |
Electrical resistivity | 23.0 °C | 1.28E-7 Ω·m Show Material materials with Electrical resistivity of 1.28E-7 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 1.3 - 2.3 % Show Material materials with Aluminium of 1.3 - 2.3 % |
Copper | 57 - 59 % Show Material materials with Copper of 57 - 59 % |
Iron | 1 % Show Material materials with Iron of 1 % |
Lead | 0.2 - 0.8 % Show Material materials with Lead of 0.2 - 0.8 % |
Manganese | 1.5 - 3 % Show Material materials with Manganese of 1.5 - 3 % |
Nickel | 1 % Show Material materials with Nickel of 1 % |
Other | Rest Zn, total 0.3 |
Silicon | 0.3 - 1.3 % Show Material materials with Silicon of 0.3 - 1.3 % |
Tin | 0.4 % Show Material materials with Tin of 0.4 % |
Technological properties
| Property | ||
|---|---|---|
| Brazing | hard brazing : wenig geeignet, soft brazing: wenig geeignet | |
| Workability | Cold forming degree between anneals: max. 15 %, general (condition): limited | |