General
Property | Temperature | Value |
---|---|---|
Density | 23.0 °C | 8.26 g/cm³ Show Supplier Material materials with Density of 8.26 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Charpy impact energy | 23.0 °C | 1.3 J Show Supplier Material materials with Charpy impact energy of 1.3 J | |
Compressive strength | 23.0 °C | 1654 MPa Show Supplier Material materials with Compressive strength of 1654 MPa | |
Elastic modulus | 23.0 °C | 128 GPa Show Supplier Material materials with Elastic modulus of 128 GPa | |
Elongation A5 | 23.0 °C | 5 % Show Supplier Material materials with Elongation A5 of 5 % | |
Fatigue strength | 23.0 °C | 330 MPa Show Supplier Material materials with Fatigue strength of 330 MPa | 100.000.000 cycles |
Hardness, HBW | 23.0 °C | 340 [-] Show Supplier Material materials with Hardness, HBW of 340 [-] | HBW 10/3000 |
Hardness, Rockwell C | 23.0 °C | 36 [-] Show Supplier Material materials with Hardness, Rockwell C of 36 [-] | |
Izod impact energy | 23.0 °C | 2.6 J Show Supplier Material materials with Izod impact energy of 2.6 J | |
Proportional limit | 23.0 °C | 586 MPa Show Supplier Material materials with Proportional limit of 586 MPa | |
Proportional limit in compression | 23.0 °C | 655 MPa Show Supplier Material materials with Proportional limit in compression of 655 MPa | |
Reduction of area | 23.0 °C | 2.5 % Show Supplier Material materials with Reduction of area of 2.5 % | |
Shear strength | 23.0 °C | 620 MPa Show Supplier Material materials with Shear strength of 620 MPa | |
Tensile strength | 23.0 °C | 1140 MPa Show Supplier Material materials with Tensile strength of 1140 MPa | |
Yield strength Rp0.5 | 23.0 °C | 1000 MPa Show Supplier Material materials with Yield strength Rp0.5 of 1000 MPa |
Thermal
Property | Temperature | Value |
---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.75E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.75E-5 1/K |
Specific heat capacity | 23.0 °C | 380 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 380 J/(kg·K) |
Thermal conductivity | 23.0 °C | 106 W/(m·K) Show Supplier Material materials with Thermal conductivity of 106 W/(m·K) |
Electrical
Property | Temperature | Value |
---|---|---|
Electrical conductivity | 23.0 °C | 2.20E+7 S/m Show Supplier Material materials with Electrical conductivity of 2.20E+7 S/m |
Specific Electrical conductivity | 22 % IACS Show Supplier Material materials with Specific Electrical conductivity of 22 % IACS |
Chemical properties
Property | Value | Comment | |
---|---|---|---|
Beryllium | 1.9 % Show Supplier Material materials with Beryllium of 1.9 % | ||
Cobalt | 0.5 % Show Supplier Material materials with Cobalt of 0.5 % | Co+Ni | |
Copper | Balance | ||
Nickel | 0.5 % Show Supplier Material materials with Nickel of 0.5 % | Co+Ni | |
Other | 0.5 % Show Supplier Material materials with Other of 0.5 % |
Technological properties
Property | ||
---|---|---|
Application areas | 2.1247 is used wherever good wear resistance or high mechanical properties are desired coupled with a good electrical or thermal conductivity, such as: Flash butt welding and butt welding, Parts for electrical components, in the plastic mould industry is sometimes used as chill plates and inserts in the moulds, cooling pins and neck rings or bottom plates for blow moulds of plastic bottles. |