General
Property | Value | Testing Standard | Condition | Comment |
---|---|---|---|---|
Coefficient of friction | 0.19 [-] Show Supplier Material materials with Coefficient of friction of 0.19 [-] | ASTM D1894 | vs Steel, Kinetic | |
0.26 [-] Show Supplier Material materials with Coefficient of friction of 0.26 [-] | ASTM D1894 | vs Steel, Static | ||
Density | 1.77 - 1.8 g/cm³ Show Supplier Material materials with Density of 1.77 - 1.8 g/cm³ | ASTM D792 | ||
1.78 g/cm³ Show Supplier Material materials with Density of 1.78 g/cm³ | ISO 1183 | dry | ||
Limiting oxygen index | 43 % Show Supplier Material materials with Limiting oxygen index of 43 % | ISO 4589-1/-2 | dry | |
Water absorption | 0.03 % Show Supplier Material materials with Water absorption of 0.03 % | Sim. to ISO 62 |
Mechanical
Property | Temperature | Value | Testing Standard | Condition | Comment |
---|---|---|---|---|---|
Compressive strength | 41.4 - 58.6 MPa Show Supplier Material materials with Compressive strength of 41.4 - 58.6 MPa | ASTM D695 | |||
Elastic modulus | 1.0 - 1.5 GPa Show Supplier Material materials with Elastic modulus of 1.0 - 1.5 GPa | ASTM D638 | |||
Elongation | 30 - 200 % Show Supplier Material materials with Elongation of 30 - 200 % | ASTM D638 | |||
50 % Show Supplier Material materials with Elongation of 50 % | ISO 527-1/-2 | dry | min. | nominal | ||
Elongation at yield | 5 - 15 % Show Supplier Material materials with Elongation at yield of 5 - 15 % | ASTM D638 | |||
10 % Show Supplier Material materials with Elongation at yield of 10 % | ISO 527-1/-2 | dry | |||
Flexural modulus | 1.0 - 1.2 GPa Show Supplier Material materials with Flexural modulus of 1.0 - 1.2 GPa | ASTM D790 | |||
Flexural strength | 20.7 - 34.5 MPa Show Supplier Material materials with Flexural strength of 20.7 - 34.5 MPa | ASTM D790 | at 5% strain | ||
Hardness, Shore D | 70 - 75 [-] Show Supplier Material materials with Hardness, Shore D of 70 - 75 [-] | ASTM D2240 | |||
Impact strength, Charpy notched, ASTM | 23 °C | 160 - 427 J/m Show Supplier Material materials with Impact strength, Charpy notched, ASTM of 160 - 427 J/m | ASTM D256 | ||
Impact strength, Charpy unnotched, ASTM | No Break at 23°C | ASTM D256 | |||
Tensile strength | 27.6 - 48.3 MPa Show Supplier Material materials with Tensile strength of 27.6 - 48.3 MPa | ASTM D638 | |||
Yield strength | 31 - 41.4 MPa Show Supplier Material materials with Yield strength of 31 - 41.4 MPa | ASTM D638 | |||
35 MPa Show Supplier Material materials with Yield strength of 35 MPa | ISO 527-1/-2 | dry |
Thermal
Property | Value | Testing Standard | Pressure | Condition | Comment | ||||
---|---|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 0.000126 - 0.000185 1/K Show Supplier Material materials with Coefficient of thermal expansion of 0.000126 - 0.000185 1/K | ASTM D696 | |||||||
Glass transition temperature | -40.6 - -38.3 °C Show Supplier Material materials with Glass transition temperature of -40.6 - -38.3 °C | ASTM D7028 | |||||||
Heat deflection temperature | 38 - 55 °C Show Supplier Material materials with Heat deflection temperature of 38 - 55 °C | ASTM D648 | 2 MPa | 248 °F/hr | |||||
46 °C Show Supplier Material materials with Heat deflection temperature of 46 °C | ISO 75-1/-2 | 2 MPa | dry | ||||||
60 - 75 °C Show Supplier Material materials with Heat deflection temperature of 60 - 75 °C | ASTM D648 | 0.45 MPa | 248 °F/hr | ||||||
Melting point | 155 - 160 °C Show Supplier Material materials with Melting point of 155 - 160 °C | ASTM D3418 | |||||||
158 °C Show Supplier Material materials with Melting point of 158 °C | ISO 11357-1/-3 | dry | 10°C/min | ||||||
Relative temperature index, electrical | 140 °C Show Supplier Material materials with Relative temperature index, electrical of 140 °C | UL 746B | |||||||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||||||
Specific heat capacity | 745 - 958 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 745 - 958 J/(kg·K) | DSC | |||||||
Thermal conductivity | 0.144 - 0.18 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.144 - 0.18 W/(m·K) | ASTM D433 | |||||||
Thermal decomposition in air | 375 °C Show Supplier Material materials with Thermal decomposition in air of 375 °C | TGA | 1% wt. loss | ||||||
Thermal decomposition in nitrogen | 410 °C Show Supplier Material materials with Thermal decomposition in nitrogen of 410 °C | TGA | 1% wt. loss | ||||||
Flammability | At thickness 0.8 mm IEC 60695-11-10: V-0 |
Electrical
Property | Value | Condition | Testing Standard |
---|---|---|---|
Volume resistivity | 2e+14 Ω·cm Show Supplier Material materials with Volume resistivity of 2e+14 Ω·cm | dry | IEC 60093 |
Rheological Properties
Property | Value | Testing Standard | Condition | Comment |
---|---|---|---|---|
Melt mass-flow rate | 4 - 18 g/10min Show Supplier Material materials with Melt mass-flow rate of 4 - 18 g/10min | ASTM D1238 | 230°C/12.5kg | |
Melt viscosity | 28 - 1600 Pa·s Show Supplier Material materials with Melt viscosity of 28 - 1600 Pa·s | ASTM D3835 | ||
Melt volume-flow rate | 7.5 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 7.5 cm³/10min | ISO 1133 | dry | 230°C/3.8kg |
Technological properties
Property |
---|