Kynar Flex® 3120-10

Alternative and trade names
PVDF
Want to keep this datasheet? Save it now in your required format

Description

Kynar Flex® resins are fluorinated thermoplastic copolymers.

Kynar Flex® 3120-10 resin is a pelletized, flexible, semi-crystalline copolymer.

Kynar Flex® 3120-10 resin is a fluid grade that can be extruded or injection molded to make final products with a 150°C rating.

Additional characteristics:

  • Excellent thermal stability
  • Excellent abrasion resistance
  • UL RTI temperature rating of 150°C
  • Impervious to UV degradation

  • This material data has been provided by Arkema High Performance Polymers.

    All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
    Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

    Ashby charts

    See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

    Properties

    General

    PropertyTemperatureValueComment

    Density

    23.0 °C

    1.78 g/cm³

    Show Supplier Material materials with Density of 1.78 g/cm³

    ISO 1183

    Limiting oxygen index

    23.0 °C

    43 %

    Show Supplier Material materials with Limiting oxygen index of 43 %

    ISO 4589-1/-2

    Water absorption

    23.0 °C

    0.03 %

    Show Supplier Material materials with Water absorption of 0.03 %

    Sim. to ISO 62

    Mechanical

    PropertyTemperatureValueComment

    Elastic modulus

    23.0 °C

    0.7 GPa

    Show Supplier Material materials with Elastic modulus of 0.7 GPa

    ISO 527-1/-2

    Elongation

    23.0 °C

    50 %

    Show Supplier Material materials with Elongation of 50 %

    min., ISO 527-1/-2, nominal

    Elongation at yield

    23.0 °C

    15 %

    Show Supplier Material materials with Elongation at yield of 15 %

    ISO 527-1/-2

    Yield strength

    23.0 °C

    27 MPa

    Show Supplier Material materials with Yield strength of 27 MPa

    ISO 527-1/-2

    Impact strength, Charpy notched

    No break @ 23°C, ISO 179/1eA

    Thermal

    PropertyTemperatureValueComment

    Glass transition temperature

    -40 °C

    Show Supplier Material materials with Glass transition temperature of -40 °C

    ISO 11357-1/-2, 10°C/min

    Heat deflection temperature, 1.80 MPa

    50 °C

    Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 50 °C

    ISO 75-1/-2

    Melting point

    165 °C

    Show Supplier Material materials with Melting point of 165 °C

    ISO 11357-1/-3, 10°C/min

    Relative temperature index, electrical

    150 °C

    Show Supplier Material materials with Relative temperature index, electrical of 150 °C

    UL 746B

    Relative temperature index, mechanical strength

    150 °C

    Show Supplier Material materials with Relative temperature index, mechanical strength of 150 °C

    UL 746B

    Specific heat capacity

    23.0 °C

    745 - 958 J/(kg·K)

    Show Supplier Material materials with Specific heat capacity of 745 - 958 J/(kg·K)

    DSC

    Thermal decomposition in air

    375 °C

    Show Supplier Material materials with Thermal decomposition in air of 375 °C

    TGA, 1% wt. loss

    Thermal decomposition in nitrogen

    410 °C

    Show Supplier Material materials with Thermal decomposition in nitrogen of 410 °C

    TGA, 1% wt. loss

    Flammability

    At thickness 1.5 mm IEC 60695-11-10: V-0, At thickness 1 IEC 60695-11-10: V-0 and yellow card available, 5V at thickness 1 mm IEC 60695-11-20: 5VA

    Rheological Properties

    PropertyValueComment

    Melt volume-flow rate

    4 cm³/10min

    Show Supplier Material materials with Melt volume-flow rate of 4 cm³/10min

    ISO 1133, 232°C/3.8kg

    Technological properties

    Property
    Application areas

    Cable Ties,Chemical Process Industry - Injection Molding