Properties
General
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Coefficient of friction | 0.12 [-] Show Supplier Material materials with Coefficient of friction of 0.12 [-] | ASTM D1894 | vs Steel, Kinetic |
0.18 [-] Show Supplier Material materials with Coefficient of friction of 0.18 [-] | ASTM D1894 | vs Steel, Static | |
Density | 1.84 - 1.88 g/cm³ Show Supplier Material materials with Density of 1.84 - 1.88 g/cm³ | ASTM D792 | |
Limiting oxygen index | 44 % Show Supplier Material materials with Limiting oxygen index of 44 % | ASTM D2863 | |
Water absorption | 0.02 % Show Supplier Material materials with Water absorption of 0.02 % | Sim. to ISO 62 |
Mechanical
| Property | Temperature | Value | Testing Standard | Condition | Comment |
|---|---|---|---|---|---|
Compressive strength | 138 - 172 MPa Show Supplier Material materials with Compressive strength of 138 - 172 MPa | ASTM D695 | |||
Elastic modulus | 3.1 - 5.2 GPa Show Supplier Material materials with Elastic modulus of 3.1 - 5.2 GPa | ASTM D638 | |||
Elongation | 0 - 20 % Show Supplier Material materials with Elongation of 0 - 20 % | ASTM D638 | |||
Elongation at yield | 0 % Show Supplier Material materials with Elongation at yield of 0 % | ASTM D638 | |||
4 % Show Supplier Material materials with Elongation at yield of 4 % | ASTM D638 | ||||
Flexural modulus | 5.5 - 6.9 GPa Show Supplier Material materials with Flexural modulus of 5.5 - 6.9 GPa | ASTM D790 | |||
Flexural strength | 138 - 207 MPa Show Supplier Material materials with Flexural strength of 138 - 207 MPa | ASTM D790 | at 5% strain | ||
Hardness, Shore D | 74 - 79 [-] Show Supplier Material materials with Hardness, Shore D of 74 - 79 [-] | ASTM D2240 | |||
Impact strength, Charpy notched, ASTM | 23 °C | 40 - 80.1 J/m Show Supplier Material materials with Impact strength, Charpy notched, ASTM of 40 - 80.1 J/m | ASTM D256 | ||
Impact strength, Charpy unnotched, ASTM | 23 °C | 267 - 534 J/m Show Supplier Material materials with Impact strength, Charpy unnotched, ASTM of 267 - 534 J/m | ASTM D256 | ||
Tensile strength | 37.9 - 55.2 MPa Show Supplier Material materials with Tensile strength of 37.9 - 55.2 MPa | ASTM D638 | |||
Yield strength | 34.5 - 55.2 MPa Show Supplier Material materials with Yield strength of 34.5 - 55.2 MPa | ASTM D638 | |||
42 MPa Show Supplier Material materials with Yield strength of 42 MPa | ISO 527-1/-2 | dry |
Thermal
| Property | Value | Testing Standard | Condition | Pressure | Comment | ||||
|---|---|---|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 3.6e-05 - 4.5e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 3.6e-05 - 4.5e-05 1/K | ASTM D696 | |||||||
4e-05 1/K Show Supplier Material materials with Coefficient of thermal expansion of 4e-05 1/K | ISO 11359-1/-2 | dry | |||||||
Glass transition temperature | -40.6 - -38.3 °C Show Supplier Material materials with Glass transition temperature of -40.6 - -38.3 °C | ASTM D7028 | |||||||
-40 °C Show Supplier Material materials with Glass transition temperature of -40 °C | ISO 11357-1/-2 | dry | 10°C/min | ||||||
Heat deflection temperature | 110 - 127 °C Show Supplier Material materials with Heat deflection temperature of 110 - 127 °C | ASTM D648 | 2 MPa | 248 °F/hr | |||||
120 °C Show Supplier Material materials with Heat deflection temperature of 120 °C | ISO 75-1/-2 | dry | 2 MPa | ||||||
132 - 149 °C Show Supplier Material materials with Heat deflection temperature of 132 - 149 °C | ASTM D648 | 0.45 MPa | 248 °F/hr | ||||||
Melting point | 165 - 170 °C Show Supplier Material materials with Melting point of 165 - 170 °C | ASTM D3418 | |||||||
170 °C Show Supplier Material materials with Melting point of 170 °C | ISO 11357-1/-3 | dry | 10°C/min | ||||||
Thermal decomposition in air | 375 °C Show Supplier Material materials with Thermal decomposition in air of 375 °C | TGA | 1% wt. loss | ||||||
Thermal decomposition in nitrogen | 410 °C Show Supplier Material materials with Thermal decomposition in nitrogen of 410 °C | TGA | 1% wt. loss | ||||||
Flammability | At thickness 1.6 mm IEC 60695-11-10: V-0, At thickness 0.8 mm IEC 60695-11-10: V-0 | ||||||||
Electrical
| Property | Value | Frequency | Testing Standard | Condition |
|---|---|---|---|---|
Dielectric constant | 28.8 - 33.5 [-] Show Supplier Material materials with Dielectric constant of 28.8 - 33.5 [-] | 1KHz | ASTM D150 | |
33 [-] Show Supplier Material materials with Dielectric constant of 33 [-] | 100Hz | IEC 60250 | dry | |
Dissipation factor | 0.06 - 0.08 [-] Show Supplier Material materials with Dissipation factor of 0.06 - 0.08 [-] | 100KHz | ASTM D150 | |
0.061 [-] Show Supplier Material materials with Dissipation factor of 0.061 [-] | 100Hz | IEC 60250 | dry | |
Volume resistivity | 1e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+11 Ω·cm | ASTM D257 | 65% RH | |
1e+13 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm | IEC 60093 | dry |
Rheological Properties
| Property | Value | Testing Standard | Condition | Comment |
|---|---|---|---|---|
Density of melt | 1.88 g/cm³ Show Supplier Material materials with Density of melt of 1.88 g/cm³ | |||
Melt mass-flow rate | 5 - 17 g/10min Show Supplier Material materials with Melt mass-flow rate of 5 - 17 g/10min | ASTM D1238 | 230°C/3.8kg | |
Melt viscosity | 800 - 1300 Pa·s Show Supplier Material materials with Melt viscosity of 800 - 1300 Pa·s | ASTM D3835 | ||
Melt volume-flow rate | 5.8 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 5.8 cm³/10min | ISO 1133 | dry | 230°C/3.8kg |
Shrinkage | 0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | ISO 294-4 | dry | |
0.7 % Show Supplier Material materials with Shrinkage of 0.7 % | ISO 294-4 | dry | Transverse |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Chemical Process Industry | |
| Processing methods | Injection Molding: | |