Orgalloy® GT 01 NAT

Alternative and trade names
PA*

Want to keep this datasheet? Save it now in your required format

Description

Orgalloy® GT 01 NAT resin is a polyamide alloy especially designed for extrusion blow molding. This natural grade offers an excellent thermal resistance, cold impact performance and barrier properties to gas.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Properties

General

Property	Value	Condition	Testing Standard
Density	1.04 g/cm³ Show Supplier Material materials with Density of 1.04 g/cm³	dry	ISO 1183

Mechanical

Property	Temperature	Value	Condition	Testing Standard	Comment
Elastic modulus		0.5 GPa Show Supplier Material materials with Elastic modulus of 0.5 GPa	cond.	ISO 527-1/-2
Elongation		50 % Show Supplier Material materials with Elongation of 50 %	cond., dry	ISO 527-1/-2	min.
Hardness, Shore D		55 [-] Show Supplier Material materials with Hardness, Shore D of 55 [-]	dry	ISO 7619-1	15 seconds
Impact strength, Charpy notched	-30 °C	21.6 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 21.6 kJ/m²	cond.	ISO 179/1eA
	23 °C	83 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 83 kJ/m²	cond.	ISO 179/1eA
Impact strength, Charpy unnotched		No Break at 23 and -30°C	cond.	ISO 179/1eU
Yield strength		24 MPa Show Supplier Material materials with Yield strength of 24 MPa	cond.	ISO 527-1/-2
		35 MPa Show Supplier Material materials with Yield strength of 35 MPa	dry	ISO 527-3
		49 MPa Show Supplier Material materials with Yield strength of 49 MPa	dry	ISO 527-2/-2

Thermal

Property	Value	Condition	Testing Standard	Comment
Melting point	220 °C Show Supplier Material materials with Melting point of 220 °C	dry	ISO 11357-1/-3	10°C/min
Vicat softening temperature	75 °C Show Supplier Material materials with Vicat softening temperature of 75 °C		ISO 306	50°C/h 50N

Rheological Properties

Property	Value	Condition	Testing Standard	Comment
Melt volume-flow rate	1.1 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 1.1 cm³/10min	dry	ISO 1133	235°C/5kg

Technological properties

Property

Application areas

Alternative Fuel Systems - CNG, LPG, LNG Lines and Tanks

Processing methods

Blow Molding:

Drying time (only necessary for bags opened for more than two hours): 4-8 hours at 80°C

Extrusion melt temperature (min-recommended-max): 250-260-270°C