Orgalloy® RS 6010 NAT

Alternative and trade names
PA6-GF10
Want to keep this datasheet? Save it now in your required format

Description

Orgalloy® RS 6010 NAT resin is a fiberglass reinforced polyamide 6 alloy designed for injection molding. This natural grade offers an outstanding dimensional stability, chemical resistance to automotive fluids and is ideal for the realization of complex parts.

This material data has been provided by Arkema Technical Polymers.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Density

1.12 g/cm³

Show Supplier Material materials with Density of 1.12 g/cm³

dry

ISO 1183

Moisture absorption

1.2 %

Show Supplier Material materials with Moisture absorption of 1.2 %

Sim. to ISO 62

Water absorption

3 %

Show Supplier Material materials with Water absorption of 3 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

3.8 GPa

Show Supplier Material materials with Elastic modulus of 3.8 GPa

cond.

ISO 527-1/-2

4.2 GPa

Show Supplier Material materials with Elastic modulus of 4.2 GPa

dry

ISO 527-1/-2

Elongation

4 %

Show Supplier Material materials with Elongation of 4 %

cond., dry

ISO 527-1/-2

nominal

Elongation at yield

3 %

Show Supplier Material materials with Elongation at yield of 3 %

cond., dry

ISO 527-1/-2

Hardness, Shore D

76 [-]

Show Supplier Material materials with Hardness, Shore D of 76 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

23 °C

7 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 7 kJ/m²

dry

ISO 179/1eA

23 °C

11 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 11 kJ/m²

cond.

ISO 179/1eA

Impact strength, Charpy unnotched

No Break at 23°C

cond.

ISO 179/1eU

Yield strength

55 MPa

Show Supplier Material materials with Yield strength of 55 MPa

dry

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardPressureComment

Heat deflection temperature

190 °C

Show Supplier Material materials with Heat deflection temperature of 190 °C

dry

ISO 75-1/-2

2 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature of 210 °C

dry

ISO 75-1/-2

0.45 MPa

Melting point

220 °C

Show Supplier Material materials with Melting point of 220 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

170 °C

Show Supplier Material materials with Vicat softening temperature of 170 °C

ISO 306

50°C/h 50N

Flammability

At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB

Electrical

PropertyValueConditionTesting StandardFrequencyComment

Comparative tracking index

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

cond.

IEC 60112

Dielectric constant

3 [-]

Show Supplier Material materials with Dielectric constant of 3 [-]

cond.

IEC 60250

100Hz

3 [-]

Show Supplier Material materials with Dielectric constant of 3 [-]

IEC 60250

1MHz

Dielectric strength

36 kV/mm

Show Supplier Material materials with Dielectric strength of 36 kV/mm

cond., dry

IEC 60243-1

Dissipation factor

0.024 [-]

Show Supplier Material materials with Dissipation factor of 0.024 [-]

cond.

IEC 60250

1MHz

0.063 [-]

Show Supplier Material materials with Dissipation factor of 0.063 [-]

cond.

IEC 60250

100Hz

Surface resistivity

1e+15 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq

cond.

IEC 60093

min.

Volume resistivity

1e+13 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm

cond.

IEC 60093

min.

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

5 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 5 cm³/10min

dry

ISO 1133

235°C/2.16kg

Shrinkage

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

dry

ISO 294-4

0.6 %

Show Supplier Material materials with Shrinkage of 0.6 %

dry

ISO 294-4

Transverse

Technological properties

Property
Application areas

Accessories

Fillers

10% Glass Fiber

Processing methods

Injection Molding:

  • Drying time (only necessary for bags opened for more than two hours): 4-8 hours at 80°C
  • Injection temperature (min-recommended-max): 260-270-280°C
  • Mould temperature (min-max): 60-80°C