Orgalloy® RS 6030 NAT

Alternative and trade names
PA6-GF30
Want to keep this datasheet? Save it now in your required format

Description

Orgalloy® RS 6030 NAT resin is a fiberglass reinforced polyamide 6 alloy designed for injection molding. This natural grade offers an outstanding dimensional stability, chemical resistance to automotive fluids and is ideal for the realization of complex parts.

This material data has been provided by Arkema Technical Polymers.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionTesting Standard

Density

1.25 g/cm³

Show Supplier Material materials with Density of 1.25 g/cm³

dry

ISO 1183

Moisture absorption

1 %

Show Supplier Material materials with Moisture absorption of 1 %

Sim. to ISO 62

Water absorption

2.3 %

Show Supplier Material materials with Water absorption of 2.3 %

Sim. to ISO 62

Mechanical

PropertyTemperatureValueConditionTesting StandardComment

Elastic modulus

8.3 GPa

Show Supplier Material materials with Elastic modulus of 8.3 GPa

cond.

ISO 527-1/-2

8.9 GPa

Show Supplier Material materials with Elastic modulus of 8.9 GPa

dry

ISO 527-1/-2

Elongation

3 %

Show Supplier Material materials with Elongation of 3 %

cond., dry

ISO 527-1/-2

Hardness, Shore D

78 [-]

Show Supplier Material materials with Hardness, Shore D of 78 [-]

dry

ISO 7619-1

15 seconds

Impact strength, Charpy notched

23 °C

16 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 16 kJ/m²

dry

ISO 179/1eA

23 °C

17 kJ/m²

Show Supplier Material materials with Impact strength, Charpy notched of 17 kJ/m²

cond.

ISO 179/1eA

Impact strength, Charpy unnotched

No Break at 23°C

cond.

ISO 179/1eU

Tensile strength

130 MPa

Show Supplier Material materials with Tensile strength of 130 MPa

cond.

ISO 527-1/-2

140 MPa

Show Supplier Material materials with Tensile strength of 140 MPa

dry

ISO 527-1/-2

Yield strength

52 MPa

Show Supplier Material materials with Yield strength of 52 MPa

cond.

ISO 527-1/-2

Thermal

PropertyValueConditionTesting StandardPressureComment

Coefficient of thermal expansion

1.9e-05 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 1.9e-05 1/K

dry

ISO 11359-1/-2

0.000126 1/K

Show Supplier Material materials with Coefficient of thermal expansion of 0.000126 1/K

dry

ISO 11359-1/-2

Transverse

Heat deflection temperature

190 °C

Show Supplier Material materials with Heat deflection temperature of 190 °C

dry

ISO 75-1/-2

2 MPa

210 °C

Show Supplier Material materials with Heat deflection temperature of 210 °C

dry

ISO 75-1/-2

0.45 MPa

Melting point

220 °C

Show Supplier Material materials with Melting point of 220 °C

dry

ISO 11357-1/-3

10°C/min

Vicat softening temperature

185 °C

Show Supplier Material materials with Vicat softening temperature of 185 °C

ISO 306

50°C/h 50N

Flammability

At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB and yellow card available

Electrical

PropertyValueConditionTesting StandardFrequencyComment

Comparative tracking index

600 V

Show Supplier Material materials with Comparative tracking index of 600 V

cond.

IEC 60112

Dielectric constant

3 [-]

Show Supplier Material materials with Dielectric constant of 3 [-]

cond.

IEC 60250

100Hz

4 [-]

Show Supplier Material materials with Dielectric constant of 4 [-]

IEC 60250

1MHz

Dielectric strength

34 kV/mm

Show Supplier Material materials with Dielectric strength of 34 kV/mm

cond., dry

IEC 60243-1

Dissipation factor

0.023 [-]

Show Supplier Material materials with Dissipation factor of 0.023 [-]

cond.

IEC 60250

1MHz

0.064 [-]

Show Supplier Material materials with Dissipation factor of 0.064 [-]

cond.

IEC 60250

100Hz

Surface resistivity

1e+15 Ω/sq

Show Supplier Material materials with Surface resistivity of 1e+15 Ω/sq

cond.

IEC 60093

min.

Volume resistivity

1e+13 Ω·cm

Show Supplier Material materials with Volume resistivity of 1e+13 Ω·cm

cond.

IEC 60093

min.

Rheological Properties

PropertyValueConditionTesting StandardComment

Melt volume-flow rate

2 cm³/10min

Show Supplier Material materials with Melt volume-flow rate of 2 cm³/10min

dry

ISO 1133

235°C/2.16kg

Shrinkage

0.2 %

Show Supplier Material materials with Shrinkage of 0.2 %

dry

ISO 294-4

0.5 %

Show Supplier Material materials with Shrinkage of 0.5 %

dry

ISO 294-4

Transverse

Technological properties

Property
Application areas

Connectors E&E

Certifications

Yellow Card

Fillers

30% Glass Fiber

Processing methods

Injection Molding:

  • Drying time (only necessary for bags opened for more than two hours): 4-8 hours at 80°C
  • Injection temperature (min-recommended-max): 260-270-280°C
  • Mould temperature (min-max): 60-80°C